A study of crack propagation in austenitic steels under creep conditions including the influence of thermal pre-ageing

被引：0
|
作者：
A. G. Gulenko
A. A. Buchatskii
B. Z. Margolin
A. D. Kashtanov
V. A. Fedorova
机构：
[1] Federal State Unitary Enterprise Central Research Institute of Structural Materials “Prometey”,
来源：
Strength of Materials | 2012年 / 44卷
关键词：
creep; crack growth rate; -integral; base metal; weld; heat-affected zone; thermal ageing;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Based on processing of a large body of experimental data obtained for austenitic steels 304 and 316, the authors have determined the coefficients for the equation of crack growth rate as a function of the C* -integral under creep conditions. To analyze applicability of this equation to Russian austenitic steels, an investigation of the crack growth rate was carried out for the base metal, weld, and heat-affected zone in steels 10Kh18N9 and 08Kh16N11M3 in the initial (austenized) state and upon a long-term thermal ageing. The authors propose a method of how to allow for thermal ageing in the calculations of the crack growth rate under creep conditions.
引用
收藏
页码：585 / 599
页数：14
相关论文
共 50 条
  • [31] EFFECT OF CATHODIC HYDROGEN CHARGING ON CRACK PROPAGATION IN AUSTENITIC STAINLESS STEELS UNDER CYCLIC LOADING.
    Misawa, Toshihei
    Nomachi, Akihiko P.
    Sugawara, Hideo
    Boshoku gijutsu, 1981, 30 (04): : 227 - 229
  • [32] Experimental study on crack propagation with pre-crack under explosion load
    Yang R.
    Su H.
    Meitan Xuebao/Journal of the China Coal Society, 2019, 44 (02): : 482 - 489
  • [33] Study on the influence of arched pre-splitting crack on cracks propagation under explosion load
    Ji, Zhe
    Su, Hong
    Li, Hongwei
    Wang, Yaofeng
    Gong, Yue
    Zhao, Taiming
    Ge, Qichao
    Yang, Bo
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2025, 136
  • [34] Thermal creep of austenitic stainless steel plate material under transient heating conditions
    Farmani, Mohammad Amin
    Heidarpour, Amin
    Zhao, Xiao-Ling
    THIN-WALLED STRUCTURES, 2022, 171
  • [35] Fatigue-creep crack propagation path in solder joints under thermal cycling
    D. R. Liu
    Yi-Hsin Pao
    Journal of Electronic Materials, 1997, 26 : 1058 - 1064
  • [36] Fatigue-creep crack propagation path in solder joints under thermal cycling
    Liu, DR
    Pao, YH
    JOURNAL OF ELECTRONIC MATERIALS, 1997, 26 (09) : 1058 - 1064
  • [37] Sintered stainless steels: Fatigue crack propagation resistance under hydrogen charging conditions
    Iacoviello, F.
    Di Cocco, V.
    CORROSION SCIENCE, 2007, 49 (05) : 2099 - 2117
  • [38] Corrosion fatigue crack growth behaviour of austenitic stainless steels under light water reactor conditions
    Seifert, H. P.
    Ritter, S.
    Leber, N. J.
    CORROSION SCIENCE, 2012, 55 : 61 - 75
  • [39] Positron microbeam study on vacancy generation caused by stress corrosion crack propagation in austenitic stainless steels
    Yabuuchi, A.
    Maekawa, M.
    Kawasuso, A.
    12TH INTERNATIONAL WORKSHOP ON SLOW POSITRON BEAM TECHNIQUES (SLOPOS12), 2011, 262
  • [40] An analytical and computational study of crack initiation under transient creep conditions
    Davies, C. M.
    O'Dowd, N. P.
    Nikbin, K. M.
    Webster, G. A.
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2007, 44 (06) : 1823 - 1843
12345