Laser micromachining of porous anodic alumina film

被引：0
|
作者：
H. Jha
T. Kikuchi
M. Sakairi
H. Takahashi
机构：
[1] Hokkaido University,Lab. of Interface Microstructure Analysis (LIMSA), Division of Materials Science and Engineering, Graduate School of Engineering
来源：
Applied Physics A | 2007年 / 88卷
关键词：
Scanning Speed; Anodic Alumina; Aluminum Substrate; Oxalic Acid Solution; Porous Anodic Alumina;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A laser direct-write process on porous anodic alumina film is carried out for the fabrication of microstructure on the film, using nanosecond, second harmonic Nd:YAG laser. Laser micromachining can be preformed in two different ways on colored and pore-sealed anodic alumina film, to generate microstructures on the film. Removal of the aluminum substrate before laser irradiation greatly improves the shape characteristics of the microstructure. The depth of microstructures can be controlled by the power and the scanning speed of the laser beam. Several structures with depths from 1 to 35 μm were fabricated on anodic alumina film with good precision and reproducibility.
引用
收藏
页码：617 / 622
页数：5
相关论文
共 50 条
  • [21] Porous anodic alumina for photonics and optoelectronics
    Gavrilov, S
    Kravtchenko, D
    Zheleznyakova, A
    Timoshenko, V
    Kashkarov, P
    Melnikov, V
    Zaitsev, G
    Golovan, L
    MICRO- AND NANOELECTRONICS 2003, 2004, 5401 : 235 - 241
  • [22] Characterization of anodic porous alumina by AFM
    Sui, YC
    Saniger, JM
    MATERIALS LETTERS, 2001, 48 (3-4) : 127 - 136
  • [23] MAGNETIC NANOCOMPOSITES IN POROUS ANODIC ALUMINA
    Khodin, A.
    Vorobyova, A.
    Outkina, E.
    PHYSICS, CHEMISTRY AND APPLICATION OF NANOSTRUCTURES, 2009, : 467 - +
  • [24] A tracer study of porous anodic alumina
    Skeldon, P.
    Thompson, G. E.
    Garcia-Vergara, S. J.
    Iglesias-Rubianes, L.
    Blanco-Pinzon, C. E.
    ELECTROCHEMICAL AND SOLID STATE LETTERS, 2006, 9 (11) : B47 - B51
  • [25] Formation process of porous anodic alumina
    Zhu, Xu-Fei
    Li, Dong-Dong
    Meng, Da-Wei
    Xiao, Ying-Hong
    Nanjing Li Gong Daxue Xuebao/Journal of Nanjing University of Science and Technology, 2006, 30 (05): : 644 - 648
  • [26] Effect of porosity on the laser induced damage threshold of porous anodic alumina films
    Wu, Shigang
    Zhang, Hongying
    Wang, Hu
    Xia, Zhi Lin
    OPTIK, 2013, 124 (18): : 3246 - 3249
  • [27] Co Filled Porous Anodic Alumina Film Fabricated on ECR-Al Film with Silicon Substrate
    Fan XueWang ChaoYang LeiDiao Dongfeng Key Laboratory of Education Ministry for Modern Design and RotorBearing SystemSchool of Mechanical EngineeringXian Jiaotong UniversityXian China
    稀有金属材料与工程, 2012, 41(S1) (S1) : 136 - 139
  • [28] Co Filled Porous Anodic Alumina Film Fabricated on ECR-Al Film with Silicon Substrate
    Xue, Fan
    Chao, Wang
    Lei, Yang
    Diao Dongfeng
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 136 - 139
  • [29] A new fabrication method of aluminum nanotube using anodic porous alumina film as a template
    Department of Chemistry, Dong-A University, Busan 604-714, Korea, Republic of
    不详
    Bull. Korean Chem. Soc., 2006, 8 (1159-1163):
  • [30] Nucleation and growth of the nanostructured anodic oxides on tantalum and niobium under the porous alumina film
    Mozalev, A
    Sakairi, M
    Saeki, I
    Takahashi, H
    ELECTROCHIMICA ACTA, 2003, 48 (20-22) : 3155 - 3170
12345