Influence of Bond Coats on the Microstructure and Mechanical Behaviors of HVOF-Deposited TiAlNb Coatings

被引：0
|
作者：
H. J. Zeng
L. Q. Zhang
J. P. Lin
X. Y. He
Y. C. Zhang
P. Jia
机构：
[1] University of Science and Technology Beijing,State Key Laboratory for Advanced Metals and Materials
[2] Beijing Langqiao Surface Technology Co.,undefined
[3] Ltd.,undefined
来源：
Journal of Thermal Spray Technology | 2012年 / 21卷
关键词：
bond strength; high velocity oxygen-fuel; porosity; thermal shock test; TiAlNb intermetallic compound;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Hot dip galvanizing has been extensively employed for corrosion protection of steel structures. However, during the process of galvanization, the corrosion in molten zinc brings many problems to galvanization industry. In this study, as a material of corrosion resistance to molten zinc intended for application in Hot-dip galvanization, HVOF Ti28.15Al63.4Nb8.25Y (at.%) coatings with different bond coats (NiCr5Al, NiCoCrAlY, CoCrAlYTaSi, and NiCr80/20) were deposited onto 316L stainless steel substrate, respectively. The influences of different bond coats on HVOF Ti28.15Al63.4Nb8.25Y coatings were investigated. The results showed that bond coat had an obvious influence on improving the mechanical properties of HVOF Ti28.15Al63.4Nb8.25Y coatings. HVOF Ti28.15Al63.4Nb8.25Y coatings with NiCoCrAlY bond coat displayed the best mechanical properties. However, bond coats had no obvious effects on the microstructure, porosity, and hardness of HVOF Ti28.15Al63.4Nb8.25Y top coatings. The effects of as-received powder morphology and grain size on the characteristics of coatings were also discussed.
引用
收藏
页码：1245 / 1256
页数：11
相关论文
共 50 条
  • [31] Microstructural, Mechanical, and Tribological Evaluation of Cu-Al-based Coatings Deposited by APS and HVOF
    Cyrus Bidmeshki
    Andre C. Liberati
    Amit Roy
    Alejandra I. Encalada
    Fadhel Ben Ettouil
    Sima A. Alidokht
    Richard R. Chromik
    Christian Moreau
    Pantcho Stoyanov
    Journal of Thermal Spray Technology, 2023, 32 : 2321 - 2335
  • [32] Mechanical properties and microstructure of WC-10Co-4Cr and WC-12Co thermal spray coatings deposited by HVOF
    Santana, Y. Y.
    La Barbera-Sosa, J. G.
    Caro, J.
    Puchi-Cabrera, E. S.
    Staia, M. H.
    SURFACE ENGINEERING, 2008, 24 (05) : 374 - 382
  • [33] Microstructure and Cavitation Erosion Resistance of HVOF Deposited WC-Co Coatings with Different Sized WC
    Ding, Xiang
    Ke, Du
    Yuan, Chengqing
    Ding, Zhangxiong
    Cheng, Xudong
    COATINGS, 2018, 8 (09):
  • [34] Microstructure and abrasive wear behaviour of FeCr-TiC coatings deposited by HVOF spraying of SHS powders
    Jones, M
    Horlock, AJ
    Shipway, PH
    McCartney, DG
    Wood, JV
    WEAR, 2001, 249 (3-4) : 246 - 253
  • [35] Influence of the microstructure of plasma deposited MCrAlY coatings on their tribological behaviour
    Li, S
    Langlade, C
    Fayeulle, S
    Treheux, D
    SURFACE & COATINGS TECHNOLOGY, 1998, 100 (1-3): : 7 - 11
  • [36] Influence of carbide grain size and crystal characteristics on the microstructure and mechanical properties of HVOF-sprayed WC-CoCr coatings
    Wang, Dafeng
    Zhang, Boping
    Jia, Chengchang
    Gao, Feng
    Yu, Yueguang
    Chu, Ke
    Zhang, Mina
    Zhao, Xiaolin
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2017, 69 : 138 - 152
  • [37] Influence of Ruthenium on the Oxidation Behavior of Platinum-Rich γ-γ' Bond Coats and Their Performance in Thermal Barrier Coatings Deposited on a Nickel-Base Superalloy
    Tawancy, H. M.
    Mohammed, A. I.
    Al-Hadhrami, L. M.
    Dafalla, H.
    Alyousef, F. K.
    OXIDATION OF METALS, 2015, 84 (5-6): : 527 - 539
  • [38] Influence of Ruthenium on the Oxidation Behavior of Platinum-Rich γ–γ′ Bond Coats and Their Performance in Thermal Barrier Coatings Deposited on a Nickel-Base Superalloy
    H. M. Tawancy
    A. I. Mohammed
    L. M. Al-Hadhrami
    H. Dafalla
    F. K. Alyousef
    Oxidation of Metals, 2015, 84 : 527 - 539
  • [39] The influence of HVOF spraying parameters on the microstructure, residual stress and cavitation resistance of FeMnCrSi coatings
    Pukasiewicz, A. G. M.
    de Boer, H. E.
    Sucharski, G. B.
    Vaz, R. F.
    Procopiak, L. A. J.
    SURFACE & COATINGS TECHNOLOGY, 2017, 327 : 158 - 166
  • [40] On the Effect of Aluminum on the Microstructure and Mechanical Properties of CrN Coatings deposited by HiPIMS
    Rodrigues Guimaraes, Monica Costa
    Noronha Marques de Castilho, Bruno Cesar
    Cunha, Carlos
    Correr, Wagner Rafael
    Mordente, Paulo
    Alvarez, Fernando
    Pinto, Haroldo Cavalcanti
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2018, 21 (03):
12345