Defects, electronic properties, and α particle energy spectrum response of the Cd0.9Mn0.1Te: V single crystal

被引:0
|
作者
Lijun Luan
Yi He
Dan Zheng
Li Gao
Haohao Lv
Pengfei Yu
Tao Wang
机构
[1] Chang’an University,School of Materials Science and Engineering
[2] Northwestern Polytechnical University,School of Materials Science and Engineering
来源
Journal of Materials Science: Materials in Electronics | 2020年 / 31卷
关键词
D O I
暂无
中图分类号
学科分类号
摘要
Cadmium manganese telluride is a promising material for fabricating room-temperature nuclear radiation detectors widely used in medical imaging, environmental protection, nuclear security detection, astrophysics, and so on. The Cd0.9Mn0.1Te: V (V: CMT) crystal examined in this work was grown through the Te solution (10% excess) vertical Bridgman method. The low-temperature photoluminescence (PL) spectra indicated that the grown crystal has good quality. A simultaneous thermal excitation current spectrum was used to characterize the effect of vanadium doping on the level defects in the crystal. The current–voltage and Hall test results showed that the crystal resistivity was (3.781–6.185) × 1010 Ω cm. The conductivity was of n type. The carrier concentration was (1.69–9.94) × 106 cm−3. The Hall mobility was (3.08–9.29) × 103 cm−2 V−1 s−1. The maximum measured ratio of the light and dark currents, when the crystal was exposed to 5 mW white light, was 11. In addition, the room-temperature electron mobility-lifetime product of the middle sample was 6.925 × 10−4 cm2 V−1 using the 241Am@5.48 MeV α particle source.
引用
收藏
页码:4479 / 4487
页数:8
相关论文
共 50 条
  • [21] OPTICAL STUDIES OF CD0.9MN0.1TE DOPED WITH AU, AS, CU, AND P ACCEPTORS
    MISIEWICZ, J
    BECLA, P
    ISAACS, ED
    WOLFF, PA
    HEIMAN, D
    RAMMOHAN, LR
    WROBEL, JM
    JOURNAL OF APPLIED PHYSICS, 1988, 63 (07) : 2396 - 2401
  • [22] Localization of exciton excitation in planar structures Cd0.9Mn0.1Te/Cd0.7Mg0.3Te
    V. F. Agekyan
    A. Yu. Serov
    N. G. Filosofov
    G. Karczewski
    Physics of the Solid State, 2009, 51 : 2401 - 2404
  • [23] Localization of exciton excitation in planar structures Cd0.9Mn0.1Te/Cd0.7Mg0.3Te
    Agekyan, V. F.
    Serov, A. Yu.
    Filosofov, N. G.
    Karczewski, G.
    PHYSICS OF THE SOLID STATE, 2009, 51 (11) : 2401 - 2404
  • [24] 稀释磁性半导体Cd0.9Mn0.1Te晶体的退火改性
    郝云霄
    孙晓燕
    张继军
    介万奇
    人工晶体学报, 2009, 38 (03) : 570 - 575
  • [25] Te溶剂-Bridgman法Cd0.9Mn0.1Te晶体生长习性研究
    郑昕
    杜园园
    王涛
    介万奇
    齐阳
    栾丽君
    人工晶体学报, 2012, 41 (02) : 306 - 311
  • [26] 钒掺杂Cd0.9Mn0.1Te晶体生长与深能级缺陷研究
    游思伟
    艾涛
    栾丽君
    稀有金属材料与工程, 2022, 51 (05) : 1873 - 1878
  • [27] 电极低温退火对Cd0.9Mn0.1Te:In/V单晶探测器电学性能的影响
    栾丽君
    李龙
    张頔
    李国海
    俞鹏飞
    段理
    硅酸盐学报, 2024, 52 (05) : 1597 - 1607
  • [28] The effective diffusion coefficient and diffusion activation energy of Cd in Cd0.9Zn0.1Te crystal
    Liu Hongtao
    Sang Wenbin
    Li Wanwan
    Zhang Bin
    Min Jiahua
    Zhan Feng
    Cao Zechun
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 (10) : 1577 - 1580
  • [29] Optical and electrical properties of indium-doped Cd0.9Zn0.1Te crystal
    Li, Qiang
    Jie, Wanqi
    Fu, Li
    Wang, Tao
    Yang, Ge
    Bai, Xuxu
    Zha, Gangqiang
    JOURNAL OF CRYSTAL GROWTH, 2006, 295 (02) : 124 - 128
  • [30] Effect of Oxygen-Related Defects on Electrical Properties of Cd0.9Zn0.1Te Semiconductor
    Yu, Haiwen
    Liu, Hongguang
    Chen, Jianquan
    Jia, Ningbo
    Wang, Miao
    Yang, Mei
    Zhang, Quanchao
    Wang, Tao
    Yang, Fan
    Jie, Wanqi
    IEEE TRANSACTIONS ON NUCLEAR SCIENCE, 2024, 71 (08) : 1996 - 2002