Development of the Technology for Producing High-Purity Al2O3 Powders Based on Raw Materials from the Ural Region

被引：0
|
作者：
I. D. Kashcheev
K. G. Zemlyanoi
A. V. Doronin
机构：
[1] Federal State Budgetary Educational Institution “Ural Federal University,
[2] ”,undefined
[3] “Hydrochromium” LLC,undefined
来源：
Refractories and Industrial Ceramics | 2020年 / 61卷
关键词：
kaolin; metakaolin; aluminum hydroxide; sulfuric acid; leaching; precipitation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The paper discusses the multipurpose use of technogenic and natural raw aluminous materials for extracting valuable components, while solving environmental issues. The authors analyzed the process of granulating kaolin, obtained from the Ural region, which involves the addition of aqueous sulfuric acid solution and subsequent firing of the granules. Sulfuric-acid leaching of kaolin-containing raw materials at various acid concentrations and precipitate production times was considered. A certification of the obtained aluminum hydroxide powders was performed.
引用
收藏
页码：192 / 195
页数：3
相关论文
共 50 条
  • [31] Submicron γ-, γ’-, θ-, and κ-Al2O3 Powders from Alkaline Waste
    V. V. Garbuz
    T. A. Silinska
    T. F. Lobunets
    O. I. Bykov
    V. B. Muratov
    T. M. Terentieva
    L. M. Kuzmenko
    V. A. Petrova
    O. O. Vasiliev
    O. I. Olifan
    T. V. Khomko
    Powder Metallurgy and Metal Ceramics, 2023, 61 : 498 - 503
  • [32] Effect of Membrane Thickness on Parameters for Producing High-Purity Hydrogen from Hydrocarbon Raw Materials in Membrane-Catalytic Devices
    A. B. Vandyshev
    V. A. Kulikov
    Chemical and Petroleum Engineering, 2023, 59 : 327 - 334
  • [33] Effect of Membrane Thickness on Parameters for Producing High-Purity Hydrogen from Hydrocarbon Raw Materials in Membrane-Catalytic Devices
    Vandyshev, A. B.
    Kulikov, V. A.
    CHEMICAL AND PETROLEUM ENGINEERING, 2023, 59 (3-4) : 327 - 334
  • [34] POLYMORPHIC TRANSITIONS OF AL2O3 OBTAINED FROM VERY PURE RAW-MATERIALS
    PROKHOROVA, GN
    SOLOMIN, NV
    BOIKO, GV
    INORGANIC MATERIALS, 1977, 13 (10) : 1500 - 1502
  • [35] Preparation of forming powders of high quality β"-Al2O3 ceramics
    Fan, ZZ
    Gu, ZH
    Chen, KG
    Xu, XH
    JOURNAL OF INORGANIC MATERIALS, 1999, 14 (01) : 36 - 42
  • [36] Measurable properties of Al2O3 ceramic injection molding raw materials
    Egesz, Adam
    Gomze, Laszlo A.
    EPITOANYAG-JOURNAL OF SILICATE BASED AND COMPOSITE MATERIALS, 2013, 65 (04): : 107 - 111
  • [37] Effect of Al2O3 raw materials on fluidity of Al2O3-coated graphite powder slurry
    Kawabata, K
    Yoshimatsu, H
    Fujii, E
    Hiragushi, K
    Osaka, A
    Miura, Y
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2001, 109 (05) : 470 - 473
  • [38] Sintering of Al2O3 ceramics based on different sizes powders
    Kulkov, Sergey N.
    Grigoriev, Mihail V.
    EPITOANYAG-JOURNAL OF SILICATE BASED AND COMPOSITE MATERIALS, 2010, 62 (03): : 66 - 69
  • [39] Aluminium self-diffusion in high-purity α-Al2O3: Comparison of Ti-doped and undoped single crystals
    Fielitz, Peter
    Ganschow, Steffen
    Kelm, Klemens
    Borchardt, Guenter
    ACTA MATERIALIA, 2020, 195 : 416 - 424
  • [40] Microstructure and hardness of two-step reverse-polarity flash sintered high-purity Al2O3 ceramics
    Yang, Shoulei
    Dai, Yujin
    Han, Ning
    Wang, Zhiyi
    Chen, Shuyue
    Wang, Yidan
    Zhang, Hanwen
    Fan, Lei
    An, Linan
    Ceramics International, 2024, 50 (21) : 41664 - 41672
12345