Dielectric relaxation in complex perovskite Ba(Bi1/2Ta1/2)O3

A new lead-free perovskite Ba(Bi1/2Ta1/2)O3 was prepared by conventional ceramic fabrication technique at 1,200 °C/4 h in air atmosphere. The crystal symmetry, space group and unit cell dimensions were determined from the experimental results using FullProf software. The crystallite size and lattice strain were estimated from Williamson-Hall approach. XRD analysis of the compound indicated the formation of a single-phase cubic structure with the space group Pm3m. EDAX and SEM studies were carried out in order to evaluate the quality and purity of the compound. Permittivity data showed a low temperature coefficient of capacitance (TCC < 4%) up to +125 °C. Complex impedance analyses suggested the dielectric relaxation to be of non-Debye type. Electric modulus studies supported the hopping type of conduction in Ba(Bi1/2Ta1/2)O3.