Fabrication of dense nanocrystalline ZrO2−3 wt. % Y2O3 by hot-isostatic pressing

被引：0
|
作者：
R. Chaim
M. Hefetz
机构：
[1] Technion–Israel Institute of Technology,Department of Materials Engineering
[2] Armament Development Authority,undefined
来源：
Journal of Materials Research | 1998年 / 13卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Amorphous to nanocrystalline ZrO2−3 wt. % Y2O3 powders were formed by chemical precipitation from mixed nitrate salt solutions. The powders were cold pressed and presintered in air for 2 to 6 h within the temperature range of 1100 °C and 1300 °C. Hot isostatic pressing was performed for 2 to 3 h within the temperature range of 1150 °C to 1350 °C in argon pressure of 150 MPa. Fully dense pellets with grain size of 22 nm to 45 nm were formed by application of low presintering temperatures.
引用
收藏
页码：1875 / 1880
页数：5
相关论文
共 50 条
  • [31] FORMATION AND HOT ISOSTATIC PRESSING OF ZRO2 SOLID-SOLUTION IN THE SYSTEM ZRO2-AL2O3
    INAMURA, S
    MIYAMOTO, H
    IMAIDA, Y
    TAKAGAWA, M
    HIROTA, K
    YAMAGUCHI, O
    JOURNAL OF MATERIALS SCIENCE, 1994, 29 (18) : 4913 - 4917
  • [32] HOT ISOSTATIC PRESSING OF TETRAGONAL ZRO2 SOLID-SOLUTION POWDERS PREPARED FROM ACETYLACETONATES IN THE SYSTEM ZRO2-Y2O3-AL2O3
    WATANABE, H
    HIROTA, K
    YAMAGUCHI, O
    INAMURA, S
    MIYAMOTO, H
    SHIOKAWA, N
    TSUJI, K
    JOURNAL OF MATERIALS SCIENCE, 1994, 29 (14) : 3719 - 3723
  • [33] Features of ZrO2–Y2O3 System Nanopowders with a Different Y2O3 Content
    S. E. Porozova
    I. V. Solnyshkov
    V. B. Kul’met’eva
    V. O. Shokov
    Refractories and Industrial Ceramics, 2015, 56 : 333 - 336
  • [34] TRANSPARENT Y2O3 BY HOT-PRESSING
    DUTTA, SK
    GAZZA, GE
    MATERIALS RESEARCH BULLETIN, 1969, 4 (11) : 791 - &
  • [35] Low-temperature fabrication of Al2O3-ZrO2 (Y2O3) nanocomposites through hot pressing of amorphous powders
    Xu, Xiaojing
    Xu, Xiqing
    Liu, Jiachen
    Hong, Wenhu
    Du, Haiyan
    Hou, Feng
    CERAMICS INTERNATIONAL, 2016, 42 (13) : 15065 - 15071
  • [36] Sintering behavior of nanocrystalline ZrO2/Y2O3 mixed ceramics analyzed with SANS
    Keiderling, U
    Winterer, M
    Benker, A
    Seydel, J
    Wiedenmann, A
    Hahn, H
    SCRIPTA MATERIALIA, 2001, 44 (8-9) : 2087 - 2091
  • [37] X-RAY DIFFRACTION STUDY OF NANOCRYSTALLINE ZrO2 - Y2O3 POWDERS
    Lamas, D. G.
    Walsoe de Reca, N. E.
    ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 1999, 55 : 20 - 20
  • [38] HOT-PRESSING OF Y2O3-STABILIZED ZRO2 WITH CR2O3 ADDITIONS
    JAYARATNA, M
    YOSHIMURA, M
    SOMIYA, S
    JOURNAL OF MATERIALS SCIENCE, 1986, 21 (02) : 591 - 596
  • [39] Ceramics based on cubic ZrO2 (Y2O3) with addition of a fused Al2O3-ZrO2 (Y2O3) eutectic
    Ordan'yan, SS
    Gudovskikh, PS
    Pigunova, AN
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2004, 45 (01) : 1 - 2
  • [40] Physicochemical Properties of Hydrothermal Nanocrystalline ZrO2–Y2O3–CeO2 Powders
    I. O. Marek
    O. K. Ruban
    V. P. Redko
    M. I. Danilenko
    S. A. Korniy
    O. V. Dudnik
    Powder Metallurgy and Metal Ceramics, 2019, 58 : 125 - 132
12345