Fatigue fracture toughness of metals and alloys. Part 2. the influence of service and manufacturing factors

被引：1

作者：

Troshchenko, V.T. ^{[1
]}

Pokrovskii, V.V. ^{[1
]}

机构：

[1] Pisarenko Institute of Problems of Strength, National Academy of Sciences of Ukraine, Kiev, Ukraine

来源：

Strength of Materials | 2003年 / 35卷 / 02期

关键词：

Fatigue fracture - Load cycle - Low cycle loading - Material damages - Metals and alloys - Plastic prestraining - Specimen dimension - Specimen sizes;

D O I：

10.1023/A:1023704625636

中图分类号：

学科分类号：

摘要：

The authors consider the influence of temperature, load cycle asymmetry, specimen size, plastic prestraining, and material damage in the course of low-cycle loading on the magnitude of fatigue fracture toughness of heat resistant, high-strength chrome-molybdenum and other steels. They analyze the degree of this influence depending on various factors varied in the process of investigation.

引用

页码：105 / 113

页数：8

共 50 条

[1] Cyclic fracture toughness of metals and alloys. Part 2. Effect of operational and processing factors
Troshchenko, V.T.
Pokrovskij, V.V.
[J]. 2003, Institut Problem Prochnosti NAN
[2] Fatigue Fracture Toughness of Metals and Alloys. Part 1. Experimental Procedures and Materials and General Principles
V. T. Troshchenko
V. V. Pokrovskii
[J]. Strength of Materials, 2003, 35 (1) : 1 - 13
[3] Nonlocalized fatigue damage of metals and alloys. Part 2. Interrelation between fatigue and inelasticity
Troshchenko V.T.
[J]. Troshchenko, V.T., 2005, Springer Science and Business Media Deutschland GmbH (37) : 443 - 459
[4] INFLUENCE OF MICROSTRUCTURE ON FATIGUE AND FRACTURE OF ALUMINIUM ALLOYS.
Staley, J.T.
[J]. Aluminium, 1979, 55 (04): : 277 - 281
[5] Cyclic fracture toughness of metals and alloys. Part 1. Procedures and materials of the study and the general mechanisms
Troshchenko, V.T.
Pokrovskij, V.V.
[J]. Problemy Prochnosti, 2003, (01): : 5 - 23
[6] Mechanical properties of Al-Li alloys. Part 2. Fatigue crack propagation
[J]. Venkateswara Rao, K.T., 1600, (05):
[7] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 2. Duration of Fatigue Crack Initiation and Propagation Stages
Troshchenko, V. T.
Khamaza, L. A.
[J]. STRENGTH OF MATERIALS, 2014, 46 (04) : 445 - 457
[8] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 2. Duration of Fatigue Crack Initiation and Propagation Stages
V. T. Troshchenko
L. A. Khamaza
[J]. Strength of Materials, 2014, 46 : 445 - 457
[9] Nonlocalized fatigue damage of metals and alloys. Part 3. Strain and energy criteria
Troshchenko V.T.
[J]. Strength of Materials, 2006, 38 (1) : 1 - 19
[10] Welding Techniques and Weldability of Nickel Alloys. Part 2.
Rudolph, G.
Hoffmann, Th.
[J]. Metall, 1987, 41 (12): : 210 - 220

← 1 2 3 4 5 →