Nonlocalized fatigue damage of metals and alloys. Part 2. Interrelation between fatigue and inelasticity

被引：6

作者：

Troshchenko V.T. ^{[1
]}

机构：

[1] Pisarenko Institute of Problems of Strength, National Academy of Sciences of Ukraine, Kiev

来源：

Troshchenko, V.T. | 2005年 / Springer Science and Business Media Deutschland GmbH卷 / 37期

关键词：

And service factors; Design; High-cycle fatigue; Inelasticity; Manufacturing;

D O I：

10.1007/s11223-005-0055-5

中图分类号：

学科分类号：

摘要：

The paper considers interrelation between the regularities in the fatigue fracture and inelastic deformation taking into account the material properties, stress gradient and concentration, specimen size, load cycle asymmetry, complex stress state, temperature, loading frequency and conditions, scatter of the test results. Analysis of the data from the literature and results of original investigations has shown that the characteristics of inelasticity, which define nonlocalized fatigue damage, can be used in studies of general regularities of the high-cycle fatigue fracture. Specific results of such analysis are presented. © 2005 Springer Science + Business Media, Inc.

引用

页码：443 / 459

页数：16

共 50 条

[1] Nonlocalized fatigue damage of metals and alloys. Part 1. Inelasticity, investigation methods, and results
Troshchenko V.T.
[J]. Strength of Materials, 2005, 37 (4) : 337 - 356
[2] Nonlocalized fatigue damage to metals and alloys
Troshchenko, V. T.
[J]. MATERIALS SCIENCE, 2006, 42 (01) : 20 - 33
[3] Nonlocalized fatigue damage of metals and alloys. Part 3. Strain and energy criteria
Troshchenko V.T.
[J]. Strength of Materials, 2006, 38 (1) : 1 - 19
[4] Nonlocalized fatigue damage to metals and alloys
V. T. Troshchenko
[J]. Materials Science, 2006, 42 : 20 - 33
[5] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 2. Duration of Fatigue Crack Initiation and Propagation Stages
Troshchenko, V. T.
Khamaza, L. A.
[J]. STRENGTH OF MATERIALS, 2014, 46 (04) : 445 - 457
[6] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 2. Duration of Fatigue Crack Initiation and Propagation Stages
V. T. Troshchenko
L. A. Khamaza
[J]. Strength of Materials, 2014, 46 : 445 - 457
[7] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 1. Crack Sizes at Fatigue Limit
V. T. Troshchenko
L. A. Khamaza
[J]. Strength of Materials, 2014, 46 : 303 - 314
[8] Interrelation between inelasticity and high-cycle fatigue of metals
Troshchenko, VT
[J]. ADVANCES IN FRACTURE RESEARCH, VOLS 1-6, 1997, : 1261 - 1272
[9] Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 1. Crack Sizes at Fatigue Limit
Troshchenko, V. T.
Khamaza, L. A.
[J]. STRENGTH OF MATERIALS, 2014, 46 (03) : 303 - 314
[10] Fatigue fracture toughness of metals and alloys. Part 2. the influence of service and manufacturing factors
Troshchenko, V.T.
Pokrovskii, V.V.
[J]. Strength of Materials, 2003, 35 (02) : 105 - 113

← 1 2 3 4 5 →