Structure and Properties of Wear-Resistant Spark-Deposited Coatings Produced with a Titanium Carbide Alloy Anode

被引：0
|
作者：
Yu. G. Tkachenko
D. Z. Yurchenko
V. F. Britun
L. P. Isaeva
V. T. Varchenko
机构：
[1] National Academy of Sciences of Ukraine,Frantsevich Institute for Problems of Materials Science
来源：
Powder Metallurgy and Metal Ceramics | 2013年 / 52卷
关键词：
electrospark strengthening; electrode material; erosion property; coating property; wear resistance;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The paper examines the phase and structure formation during hot pressing of titanium carbide electrode materials as well as the structurization and properties of spark-deposited coatings on steel substrates. The influence of the operating current used for erosion processing on the phase composition and hardness of the coatings is established. It is shown that the electrode materials with a certain composition and structure enable the electrospark deposition of 100 μm-thick coatings with hardness to 14 GPa. The mass of the material deposited on a steel substrate is three times higher than that formed using standard titanium carbide alloy TN20. The wear resistance of the coatings in abrasive and dry sliding friction is high, hence they may be recommended for protection of steel parts for severe wear applications.
引用
收藏
页码：306 / 313
页数：7
相关论文
共 50 条
  • [21] Spark anodizing of β-Ti alloy for wear-resistant coating
    Habazaki, H.
    Onodera, T.
    Fushimi, K.
    Konno, H.
    Toyotake, K.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (21): : 8730 - 8737
  • [22] Laser cladding for wear-resistant cobalt base alloy and tungsten carbide composite coatings
    Chen, Yong-Chwang
    Chiang, Kwo-An
    JOURNAL OF THE CHINESE INSTITUTE OF ENGINEERS, 2006, 29 (03) : 423 - 431
  • [23] FORMATION OF THE INCREASED WEAR-RESISTANT PROPERTIES OF HARDOX 450 STEEL BY DEPOSITED COATINGS
    Konovalov, S. V.
    Kormyshev, V. E.
    Kapralov, E. V.
    Ivanov, Y. F.
    Zavatski, O. V.
    Gromov, V. E.
    XIX INTERNATIONAL SCIENTIFIC CONFERENCE ON METALLURGY: TECHNOLOGIES, INNOVATION, QUALITY (METALLURGY2015), 2016, 150
  • [24] Abrasive wear of ZrB2-containing spark-deposited and combined coatings on titanium alloy. II. Nonfixed-abrasive wear of ZrB2-containing coatings
    Podchernyaeva, I. A.
    Panasyuk, A. D.
    Panashenko, V. M.
    Grigor'ev, O. N.
    Dukhota, A. I.
    Zhiginas, V. V.
    POWDER METALLURGY AND METAL CERAMICS, 2009, 48 (7-8) : 435 - 440
  • [25] Abrasive wear of ZrB2-containing spark-deposited and combined coatings on titanium alloy. II. Nonfixed-abrasive wear of ZrB2-containing coatings
    I. A. Podchernyaeva
    A. D. Panasyuk
    V. M. Panashenko
    O. N. Grigor’ev
    A. I. Dukhota
    V. V. Zhiginas
    Powder Metallurgy and Metal Ceramics, 2009, 48 : 435 - 440
  • [26] Specific Features of the Formation of Wear-Resistant Titanium-Carbide Coatings by the Method of Electrophoretic Deposition
    H. А. Bahlyuk
    L. M. Apinins’ka
    N. M. Verheles
    N. O. Us’kova
    O. V. Bezdorozhev
    Materials Science, 2015, 51 : 37 - 43
  • [27] Specific Features of the Formation of Wear-Resistant Titanium-Carbide Coatings by the Method of Electrophoretic Deposition
    Bahlyuk, H. D.
    Apinins'ka, L. M.
    Verheles, N. M.
    Us'kova, N. O.
    Bezdorozhev, O. V.
    MATERIALS SCIENCE, 2015, 51 (01) : 37 - 43
  • [28] Properties of Wear-Resistant Composite Coatings Produced by High-Speed Boronizing
    V. P. Lyalyakin
    V. F. Aulov
    A. V. Ishkov
    I. N. Kravchenko
    Yu. A. Kuznetsov
    Journal of Machinery Manufacture and Reliability, 2022, 51 : 134 - 142
  • [29] Wear-resistant electrophoretic deposition (EPD) layer of titanium carbide
    Gorji, M. R.
    Sanjabi, S.
    Edtmaier, C.
    Katsich, C.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 806 : 1323 - 1338
  • [30] WEAR-RESISTANT MULTICOMPONENT CARBIDE COATINGS BASED ON HARD ALLOYS
    VOROSHNIN, LG
    BORISENOK, GV
    POBEREZHNYI, SV
    VITYAZ, NA
    METAL SCIENCE AND HEAT TREATMENT, 1987, 29 (3-4) : 217 - 221
12345