Fabrication and Characterization of Poly(L-lactic Acid) Fiber Mats Using Centrifugal Spinning

被引：0
|
作者：
Richard Patlan
Joscelyn Mejias
Zachary McEachin
Alfonso Salinas
Karen Lozano
机构：
[1] University of Texas-Rio Grande Valley,Mechanical Engineering Department
来源：
Fibers and Polymers | 2018年 / 19卷
关键词：
Nanofibers; Centrifugal spinning; Polylactic acid;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Polylactic acid (PLA) fine fibers and multi walled carbon nanotube (MWCNT) reinforced PLA fine fiber composites were developed utilizing a centrifugal spinning process. Chloroform and chloroform combined with dimethylformamide (DMF) were used to prepare solutions with varying concentrations of PLA and MWCNTs. The optimum spinning conditions to produce PLA fibers and its composites were determined. The morphology of the fibers was analyzed using scanning electron microscopy. In addition, X-ray diffraction analysis and thermo-physical characterization was conducted using thermogravimetric analysis and differential scanning calorimetry. PLA fibers with an average diameter of 481 nanometers and PLA/MWCNT fibers with an average diameter of 358 nanometers were obtained. A decrease in the crystallinity of the fibers was observed when compared to bulk PLA values.
引用
收藏
页码：1271 / 1277
页数：6
相关论文
共 50 条
  • [21] Modification of poly(L-lactic acid) with L-lactic acid citric acid oligomers
    Jiang, Yan
    Bai, Yun
    Chen, Man
    Yao, Fanglian
    Zhang, Haiyue
    Yao, Kang De
    E-POLYMERS, 2006,
  • [22] Fabrication of piezoelectric poly(l-lactic acid)/BaTiO3 fibre by the melt-spinning process
    Hyun Ju Oh
    Do-Kun Kim
    Young Chan Choi
    Seung-Ju Lim
    Jae Bum Jeong
    Jae Hoon Ko
    Wan-Gyu Hahm
    Sang-Woo Kim
    Yongju Lee
    Hyeok Kim
    Byeong Jin Yeang
    Scientific Reports, 10
  • [23] Fabrication of piezoelectric poly(l-lactic acid)/BaTiO3 fibre by the melt-spinning process
    Oh, Hyun Ju
    Kim, Do-Kun
    Choi, Young Chan
    Lim, Seung-Ju
    Jeong, Jae Bum
    Ko, Jae Hoon
    Hahm, Wan-Gyu
    Kim, Sang-Woo
    Lee, Yongju
    Kim, Hyeok
    Yeang, Byeong Jin
    SCIENTIFIC REPORTS, 2020, 10 (01)
  • [24] Conformational differences of poly(L-lactic acid) and poly(D,L-lactic acid) in dilute solutions
    Pavlov, G. M.
    Dommes, O. A.
    Aver'yanov, I. V.
    Kolbina, G. F.
    Okatova, O. V.
    Korzhikov, V. A.
    Dobrodumov, A. V.
    Tennikova, T. B.
    DOKLADY CHEMISTRY, 2015, 465 : 261 - 264
  • [25] In vitro degradation of poly(L-lactic acid) fibers produced by melt spinning
    Pegoretti, A
    Fambri, L
    Migliaresi, C
    JOURNAL OF APPLIED POLYMER SCIENCE, 1997, 64 (02) : 213 - 223
  • [26] Fabrication and characterization of poly(L-lactic acid) gels induced by fibrous complex crystallization with solvents
    Matsuda, Yasuhiro
    Fukatsu, Akinobu
    Wang, Yangyang
    Miyamoto, Kazuaki
    Mays, Jimmy W.
    Tasaka, Shigeru
    POLYMER, 2014, 55 (16) : 4369 - 4378
  • [27] Conformational differences of poly(L-lactic acid) and poly(D,L-lactic acid) in dilute solutions
    G. M. Pavlov
    O. A. Dommes
    I. V. Aver’yanov
    G. F. Kolbina
    O. V. Okatova
    V. A. Korzhikov
    A. V. Dobrodumov
    T. B. Tennikova
    Doklady Chemistry, 2015, 465 : 261 - 264
  • [28] Fabrication and degradation of poly(L-lactic acid) scaffolds with wool keratin
    Li, Jiashen
    Li, Yi
    Li, Lin
    Mak, Arthur F. T.
    Ko, Frank
    Qin, Ling
    COMPOSITES PART B-ENGINEERING, 2009, 40 (07) : 664 - 667
  • [29] Fabrication and crystallization behavior of hollow poly(l-lactic acid) nanofibers
    Samanta, Pratick
    Srivastava, Rajiv
    Nandan, Bhanu
    POLYMER CRYSTALLIZATION, 2020, 3 (05)
  • [30] Poly (D,L-lactic acid) homopolymers: Synthesis and characterization
    Kaitian, X
    Kozluca, A
    Denkbas, EB
    Piskin, E
    TURKISH JOURNAL OF CHEMISTRY, 1996, 20 (01): : 43 - 53
12345