Structure, microstructure, and thermopower of highest manganese silicide crystals grown from zinc solution-melt

被引：0
|
作者：
F. Yu. Solomkin
V. K. Zaitsev
N. F. Kartenko
A. S. Kolosova
A. Yu. Samunin
G. N. Isachenko
机构：
[1] Russian Academy of Sciences,Ioffe Physicotechnical Institute
来源：
Technical Physics | 2008年 / 53卷
关键词：
72.20.Pa;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
MnSi1.71–1.75 single crystals are grown using the combination of solidification from solution-melt and the Bridgman crystal growth technique. The single crystals represent tetrahedral bipyramids and correspond to the highest manganese silicide (HMS) modification with lattice parameters a = b = 5.52(1) Å and c = 65.7(8) Å. The thermopower measured between the parallel faces of these single crystals is anomalously high for plain HMS (180–190 μV/K).
引用
收藏
页码：800 / 801
页数：1
相关论文
共 50 条
  • [31] Block (mosaic) structure as an indicator for cooling of crystals grown from a melt
    B. G. Ivanov
    E. S. Kaeva
    Crystallography Reports, 2005, 50 : S22 - S27
  • [32] MORPHOLOGY OF DIAMOND STRUCTURE CRYSTALS (SI AND GE) GROWN FROM MELT
    BORLE, WN
    BAGAI, RK
    SETH, GL
    INDIAN JOURNAL OF PURE & APPLIED PHYSICS, 1976, 14 (05) : 394 - 395
  • [33] DEFECT STRUCTURE IN EUS SINGLE-CRYSTALS GROWN FROM MELT
    CHANG, PH
    STRUNK, H
    HERZ, R
    APPLIED PHYSICS, 1979, 18 (01): : 29 - 33
  • [34] STRUCTURE PERFECTION OF SOME MOLECULAR-CRYSTALS GROWN FROM THE MELT
    NAUMOWICZ, P
    SZARRAS, S
    KRISTALL UND TECHNIK-CRYSTAL RESEARCH AND TECHNOLOGY, 1980, 15 (08): : 973 - 976
  • [35] A COMPARISON OF THE MORPHOLOGY OF META-CHLORONITROBENZENE CRYSTALS GROWN FROM SOLUTION AND FROM THE MELT
    CHEN, BD
    GARSIDE, J
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1991, 24 (02) : 131 - 134
  • [36] MEASUREMENT OF DISORIENTATIONS BETWEEN ADJACENT SUBGRAINS IN ZINC SINGLE CRYSTALS GROWN FROM MELT
    ZASIMCHU.IK
    OVSIENKO, DE
    SOVIET PHYSICS CRYSTALLOGRAPHY, USSR, 1966, 11 (02): : 292 - &
  • [37] FORMATION OF DEFECTS IN ZINC SELENIDE CRYSTALS GROWN FROM MELT UNDER ARGON PRESSURE
    KIKUMA, I
    FURUKOSHI, M
    JOURNAL OF CRYSTAL GROWTH, 1978, 44 (04) : 467 - 472
  • [38] Inhomogeneity of dielectric properties of cadmium zinc-telluride crystals grown from melt
    Poluboiarov, O. O.
    Chugai, O. N.
    Voloshin, O. O.
    Zherebyatiev, D. P.
    Oleynick, S. V.
    Sulima, S. V.
    FUNCTIONAL MATERIALS, 2016, 23 (03): : 378 - 381
  • [39] Structure of metal single crystals grown in various crystallographic directions from melt
    Fedorov, OP
    Zhivolub, EL
    CRYSTALLOGRAPHY REPORTS, 1998, 43 (05) : 877 - 883
  • [40] CRYSTAL-STRUCTURE OF ZNSE CRYSTALS GROWN FROM THE MELT UNDER PRESSURE
    KIKUMA, I
    FURUKOSHI, M
    JOURNAL OF CRYSTAL GROWTH, 1983, 63 (02) : 410 - 412
12345