Improvement of Properties of High-Strength Cast Irons by Surfacing a Metal with Globular Graphite

被引：0

作者：

T. P. Govorun

E. A. Belous

A. I. Lyubich

机构：

[1] Sumy State University,

来源：

Metal Science and Heat Treatment | 2018年 / 59卷

关键词：

high-strength cast iron; structural materials; surfacing; elongation; hardness; conventional yield strength; globular graphite; ultimate tensile strength; alloying composition; microstructure;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The possibility of sparing reconditioning of parts and mechanisms produced from high-strength cast iron by surfacing a metal identical to the base one but containing no scarce and expensive elements is studied. The chemical composition of the coating is determined experimentally. The mechanical properties of the deposited metal are determined. The results of the experiment are analyzed, and the composition of the powder wire blend providing formation of a ferrite-pearlite structure and globular graphite in the surfaced metal is determined. The structural components of the deposited metal are described. The optimum content of calcium in the cast iron with structurally free globular graphite is specified.

引用

页码：675 / 681

页数：6

共 50 条

[41] High-strength cast irons used for manufacturing parts of VAZ passenger cars
Kitaigora, NI
METAL SCIENCE AND HEAT TREATMENT, 1996, 38 (9-10) : 435 - 436
[42] HIGH-STRENGTH HIGH TOUGHNESS COMPACTED GRAPHITE CAST-IRON
HSU, CH
LEE, SC
MATERIALS SCIENCE AND TECHNOLOGY, 1995, 11 (08) : 765 - 775
[43] HIGH-STRENGTH BAINITIC CAST-IRON WITH SPHEROIDAL GRAPHITE
DORAZIL, E
BARTA, B
CRHAK, J
MUNSTEROVA, E
METAL SCIENCE AND HEAT TREATMENT, 1978, 20 (7-8) : 532 - 535
[44] EFFECT OF PHOSPHORUS ON THE MECHANICAL-PROPERTIES OF HIGH-STRENGTH CAST IRONS MODIFIED WITH ALLOY ZHKMK-6
KABINOV, DA
METAL SCIENCE AND HEAT TREATMENT, 1981, 23 (7-8) : 487 - 488
[45] Cyclic Crack Resistance of Grey and High-Strength Cast Irons with Increased Phosphorus Content
I. M. Andreiko
H. I. Slyn'ko
O. P. Ostash
I. P. Volchok
Materials Science, 2000, 36 : 849 - 856
[46] Cyclic Crack Resistance of High-Strength Cast Irons at the Stages of Initiation and Growth of a Macrocrack
O. P. Ostash
I. M. Andreiko
Materials Science, 2001, 37 : 65 - 72
[47] Cyclic crack resistance of high-strength cast irons at the stages of initiation and growth of a macrocrack
Ostash, OP
Andreiko, IM
MATERIALS SCIENCE, 2001, 37 (01) : 65 - 72
[48] Enhancement of the resistance of cold-resistant high-strength cast irons to brittle fracture
Ostash, OP
Dronyuk, MM
Andreiko, IM
Kostyk, EM
MATERIALS SCIENCE, 1996, 32 (06) : 699 - 707
[49] EFFECT OF THE SHAPE OF GRAPHITE AND OF THE DISPERSITY OF MARTENSITE ON THE MECHANICAL PROPERTIES OF HIGH-STRENGTH CAST IRON.
Yakovlev, F.I.
Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1986, 28 (5-6): : 378 - 380
[50] Cyclic crack resistance of grey and high-strength cast irons with increased phosphorus content
Andreiko, IM
Slyn'ko, HI
Ostash, OP
Volchok, IP
MATERIALS SCIENCE, 2000, 36 (06) : 849 - 856

← 1 2 3 4 5 →