Synthesis of a minute SiC product from polyvinylsilane with radiation curing Part I Radiation curing of polyvinylsilane

被引:0
|
作者
A. Idesaki
M. Sugimoto
S. Tanaka
M. Narisawa
K. Okamura
M. Itoh
机构
[1] Japan Atomic Energy Research Institute,Takasaki Radiation Chemistry Research Establishment
[2] Osaka Prefecture University,Department of Metallurgy and Materials Science, Graduate School of Engineering
[3] Fukushima National College of Technology,Department of Chemistry and Biochemistry
来源
关键词
Nitrogen; Radiation; Polymer; Atmosphere; Mold;
D O I
暂无
中图分类号
学科分类号
摘要
Irradiation effect of γ-ray on polyvinylsilane (PVS), which is a liquid organosilicon polymer, was investigated and the optimum curing condition to synthesize a minute SiC product with radiation curing was discussed. Room temperature and liquid nitrogen temperature (77 K) were examined as the irradiation temperature. In both cases, the cured PVS maintaining its formed shape could be obtained by γ-ray irradiation under vacuum, and the cured PVS in solid state at room temperature was obtained by irradiation with dose of above 3–4 MGy. It was found that the efficiency of crosslinking in case of the irradiation at room temperature is higher than that in case of irradiation at 77 K. The PVS injected into a mold was irradiated by γ-ray with dose of 3.6 MGy at room temperature under vacuum, and pyrolyzed at 1273 K in Ar gas atmosphere. As a result, minute SiC products which had similar shapes to the mold and the sizes of 30–60 μm were obtained.
引用
收藏
页码:5689 / 5694
页数:5
相关论文
共 50 条
  • [1] Synthesis of a minute SiC product from polyvinylsilane with radiation curing - Part I - Radiation curing of polyvinylsilane
    Idesaki, A
    Sugimoto, M
    Tanaka, S
    Narisawa, M
    Okamura, K
    Itoh, M
    [J]. JOURNAL OF MATERIALS SCIENCE, 2004, 39 (18) : 5689 - 5694
  • [2] Synthesis of a minute SiC product from polyvinylsilane with radiation curing: Part II - Ceramization process of radiation cured polyvinylsilane
    Idesaki, Akira
    Sugimoto, Masaki
    Yoshikawa, Masahito
    Tanaka, Shigeru
    Narisawa, Masaki
    Okamura, Kiyohito
    Itoh, Masayoshi
    [J]. JOURNAL OF MATERIALS SCIENCE, 2007, 42 (01) : 130 - 135
  • [3] Synthesis of a minute SiC product from polyvinylsilane with radiation curing: Part II—Ceramization process of radiation cured polyvinylsilane
    Akira Idesaki
    Masaki Sugimoto
    Masahito Yoshikawa
    Shigeru Tanaka
    Masaki Narisawa
    Kiyohito Okamura
    Masayoshi Itoh
    [J]. Journal of Materials Science, 2007, 42 : 130 - 135
  • [4] Radiation curing of polyvinylsilane as a precursor for SiC-based material
    Idesaki, A
    Sugimoto, M
    Tanaka, S
    Narisawa, M
    Okamura, K
    Itoh, M
    [J]. ADVANCED CERAMICS AND COMPOSITES, 2003, 247 : 129 - 132
  • [5] Formation of silicone carbide membrane by radiation curing of polycarbosilane and polyvinylsilane and its gas separation up to 250°C
    Wach, Radoslaw A.
    Sugimoto, Masaki
    Yoshikawa, Masahito
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (01) : 275 - 278
  • [6] Application of electron beam curing for silicon carbide fiber synthesis from blend polymer of polycarbosilane and polyvinylsilane
    Idesaki, A
    Narisawa, M
    Okamura, K
    Sugimoto, M
    Morita, Y
    Seguchi, T
    Itoh, M
    [J]. RADIATION PHYSICS AND CHEMISTRY, 2001, 60 (4-5) : 483 - 487
  • [7] SYNTHESIS OF A POROUS SiC MATERIAL FROM POLYCARBOSILANE BY DIRECT FOAMING AND RADIATION CURING
    Idesaki, Akira
    Sugimoto, Masaki
    Yoshikawa, Masahito
    [J]. Innovative Processing and Manufacturing of Advanced Ceramics and Composites II, 2014, 243 : 61 - 69
  • [8] Synthesis of SiC-based fibers derived from hybrid polymer of polycarbosilane and polyvinylsilane
    Idesaki, A
    Narisawa, M
    Okamura, K
    Sugimoto, M
    Seguchi, T
    Itoh, M
    [J]. NOVEL SYNTHESIS AND PROCESSING OF CERAMICS, 1999, 159-1 : 107 - 111
  • [9] Fine silicon carbide fibers synthesized from polycarbosilane-polyvinylsilane polymer blend using electron beam curing
    A. Idesaki
    M. Narisawa
    K. Okamura
    M. Sugimoto
    Y. Morita
    T. Seguchi
    M. Itoh
    [J]. Journal of Materials Science, 2001, 36 : 357 - 362
  • [10] Fine silicon carbide fibers synthesized from polycarbosilane-polyvinylsilane polymer blend using electron beam curing
    Idesaki, A
    Narisawa, M
    Okamura, K
    Sugimoto, M
    Morita, Y
    Seguchi, T
    Itoh, M
    [J]. JOURNAL OF MATERIALS SCIENCE, 2001, 36 (02) : 357 - 362