Study on Hydrogen-Assisted Cracking in High-Strength Steels by Using the Granjon Implant Test

被引：13

作者：

Yadav U. ^{[1
]}

Pandey C. ^{[1
]}

Saini N. ^{[1
]}

Thakre J.G. ^{[1
]}

Mahapatra M.M. ^{[2
]}

机构：

[1] Department of Mechanical and Industrial Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667, Uttrakhand

[2] School of Mechanical Sciences, Indian Institute of Technology Bhubaneswar, Bhubaneswar, 751013, Odisha

来源：

Metallography, Microstructure, and Analysis | 2017年 / 6卷 / 3期

关键词：

Heat-affected zone; Hydrogen-assisted cracking; Implant test; Lower critical stress; Shielded metal arc welding;

D O I：

10.1007/s13632-017-0351-z

中图分类号：

学科分类号：

摘要：

In present research work, the modified Granjon implant test was performed to evaluate the susceptibility of AISI 8620 and AISI 304 steels toward the hydrogen-assisted cracking. To measure the diffusible hydrogen level (HD) in deposited metal, glycerin method was employed. Shielded metal arc welding process with basic type electrode was used to deposit the metal. The hydrogen was intentionally introduced for the plate of the material AISI 304 by using an oil of grade Society of Automotive Engineers 10, which is of very low viscosity. The heat-affected zone susceptibility was quantified by finding the lower critical stress for a measured hydrogen content. © 2017, Springer Science+Business Media New York and ASM International.

引用

页码：247 / 257

页数：10

共 50 条

[41] Mesoscale modeling of hydrogen-assisted cracking in duplex stainless steels
Mente, Tobias
Boellinghaus, Thomas
WELDING IN THE WORLD, 2014, 58 (02) : 205 - 216
[42] RECENT OBSERVATION OF HYDROGEN-INDUCED CRACKING OF HIGH-STRENGTH STEELS
McMahon, C. J., Jr.
Liu, Xinyu
Kameda, Jun
Morgan, Michael J.
EFFECTS OF HYDROGEN ON MATERIALS, 2009, : 46 - +
[43] HYDROGEN INDUCED CRACKING SUSCEPTIBILITY OF HIGH-STRENGTH LINE PIPE STEELS
MATSUMOTO, K
KOBAYASHI, Y
UME, K
MURAKAMI, K
TAIRA, K
ARIKATA, K
CORROSION, 1986, 42 (06) : 337 - 345
[44] Effect of fatigue pre-loading on mixed-mode hydrogen-assisted cracking initiation in high-strength steel
Toribio, J
Ovejero, E
Khrain, V
FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2243 - 2248
[45] Hydrogen-Assisted Cracking in GMA Welding of High-Strength Structural Steel-A New Look into This Issue at Narrow Groove
Schaupp, Thomas
Schroeder, Nina
Schroepfer, Dirk
Kannengiesser, Thomas
METALS, 2021, 11 (06)
[46] EFFECT OF LOADING MODE ON THE HYDROGEN-ASSISTED FRACTURE OF AN ULTRA HIGH-STRENGTH STEEL
TAKEMOTO, M
CORROSION, 1986, 42 (10) : 585 - 592
[47] Effect of grain size on the hydrogen-assisted cracking in duplex stainless steels
Chou, Shyan-Liang
Tsai, Wen-Ta
Materials Science and Engineering: A, 1999, 270 (02): : 219 - 224
[48] Effect of grain size on the hydrogen-assisted cracking in duplex stainless steels
Chou, SL
Tsai, WT
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 270 (02): : 219 - 224
[49] Stress corrosion cracking of high-strength steels
Ramamurthy, Sridhar
Atrens, Andrej
CORROSION REVIEWS, 2013, 31 (01) : 1 - 31
[50] Stress corrosion cracking of high-strength steels
Li, HL
Chu, WY
Gao, KW
Qiao, LJ
STEEL RESEARCH, 2001, 72 (09): : 366 - 370

← 1 2 3 4 5 →