Creating Weldable High-Strength Structural Steel with Nanostructuring

被引:1
|
作者
Oryshchenko A.S. [1 ]
机构
[1] Gorynin Prometei Central Research Institute of Structural Materials, Kurchatov Institute, St. Petersburg
关键词
carbon equivalent; fragmentation; low-temperature steel; plastic deformation; plastometer; structure; thermomechanical treatment; yield point;
D O I
10.3103/S0967091217110080
中图分类号
学科分类号
摘要
Exploitation of the Arctic calls for the creation of economical high-strength steel capable of operating at low temperatures. Research shows that, to that end, means of controlling the steel structure must be identified, so as to create quasi-isotropic fragmented nanostructure within the metal. The formation of finegrain structure is possible by a combination of intense plastic deformation with recrystallization and phase transformations. To confirm the theoretical and experimental preconditions for this process, experiments are conducted on the Gleeble-3800 instrument and a Kvarto-800 four-high rolling mill. Experimental steel melts with a carbon equivalent Cequ = 0.44–0.87% are investigated. In simulation on the Gleeble-3800 instrument, compressive deformation is applied in two stages: roughing at 1080–1100°C; and finishing at 950 and 820°C. That simulates the deformation cycle in industrial Kvarto-5000 four-high mills. The grain size in the steel is decreased from 6.5 to 2.2 μm after deformation at 950°C and 1.1 μm after deformation at 810°C. Fragments smaller than 500 nm constitute 20–37% of the steel structure. In the steel with Cequ = 0.44–0.65%, the yield point is 500–700 MPa, which is 40% greater than the standard values. In the steel with Cequ = 0.65–0.87%, the yield point is 700–1150 MPa. These values are obtained with increase in nickel content in the steel to 3%. At higher Ni concentrations, no improvement in yield point is seen. After rolling on the Kvarto-800 mill, with Cequ = 0.60–0.87% in one pass (with 70% reduction) at 1100°C and direct quenching with subsequent tempering at 600°C, the yield point is 1060 MPa. In this case, variation in the Ni content and Cequ has little influence on the yield point. The steel consists of bainite (mean grain size 6.9–8.3 μm), with a large dislocation density (1–2) × 1015 m–2 and considerable fragmentation within the grain. On the basis of the new technology, a group of low-temperature steels with yield points of 270–690 MPa and Cequ = 0.32–0.65% is created. The thickness of the steel sheet is up to 130 mm; it may operate at temperatures as low as –60°C. Such steel may be used for atomic icebreakers, other Arctic vessels, and fixed and floating drilling platforms for oil and gas extraction from Russia’s Arctic shelf. This research demonstrates the possibility of creating structural steels with relatively little alloying (up to 20–30%) and with standardized chemical composition. © 2017, Allerton Press, Inc.
引用
收藏
页码:717 / 721
页数:4
相关论文
共 50 条
  • [21] Weldable high-strength steels: Challenges and engineering applications
    David APorter
    谷森
    机械制造文摘(焊接分册), 2015, (04) : 26 - 28
  • [22] EFFECT OF ZIRCONIUM ON TOUGHNESS OF WELDABLE HIGH-STRENGTH STRUCTURAL STEELS CONTAINING NIOBIUM OF VANADIUM
    HEISTERKAMP, F
    LAUTERBO.D
    MEYER, L
    STRASSBU.C
    STAHL UND EISEN, 1970, 90 (22): : 1255 - +
  • [23] Hydrogen Degradation of High-Strength Weldable Steels in Seawater
    J. Cwiek
    K. Nikiforov
    Materials Science, 2004, 40 : 831 - 835
  • [24] Hydrogen degradation of high-strength weldable steels in seawater
    Cwiek, J
    Nikiforov, K
    MATERIALS SCIENCE, 2004, 40 (06) : 831 - 835
  • [25] IMPROVEMENT OF PROPERTIES OF HIGH-STRENGTH WELDABLE ALZNMG ALLOYS
    GRUHL, W
    CORDIER, H
    OSTERMAN.F
    SCHOER, H
    METALL, 1973, 27 (03): : 211 - 219
  • [26] METHODS FOR PREVENTING STRESS-CORROSION CRACKING OF HIGH-STRENGTH, WELDABLE STAINLESS-STEEL
    LASHCHEVSKII, VB
    GURVICH, LY
    BATRAKOV, VP
    KOZHEUROVA, NS
    MOLOTOVA, VA
    SHVARTS, MM
    PROTECTION OF METALS, 1978, 14 (02): : 106 - 109
  • [27] FATIGUE STRENGTH OF A WELDABLE HIGH STRENGTH MARTENSITIC STAINLESS STEEL
    KALTENHA.RH
    LOVEJOY, PT
    WELDING JOURNAL, 1967, 46 (09) : S391 - &
  • [28] Blast resistance of high-strength structural steel welds
    Th. E. Falkenreck
    Th. Boellinghaus
    Welding in the World, 2016, 60 : 475 - 483
  • [29] DEVELOPMENT OF HIGH-STRENGTH WELDABLE RAIL STEELS .3. METALLURGICAL PROPERTIES AND RESULTS OF A FIELD-TEST OF HIGH-STRENGTH WELDABLE RAIL STEELS
    KAGEYAMA, H
    SUGINO, K
    MASUMOTO, H
    HATTORI, M
    MATSUBARA, E
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (05) : B149 - B149
  • [30] Experimental Investigation of High-Strength Structural Steel Welds
    Ismar, Hajro
    Burzic, Zijah
    Kapor, Nenad J.
    Kokelj, Tugomir
    STROJNISKI VESTNIK-JOURNAL OF MECHANICAL ENGINEERING, 2012, 58 (06): : 422 - 428