Damage and Fracture of VT22 Titanium Alloy in Static Tension After the Application of Additional Pulse Loading

被引：0
|
作者：
P. O. Marushchak
I. V. Konovalenko
M. G. Chausov
A. P. Pylypenko
机构：
[1] Ternopil Ivan Puluj Technical University,
[2] Ukrainian National University of Bioresources and Nature Management,undefined
来源：
Strength of Materials | 2017年 / 49卷
关键词：
degradation; damage; deformation; micromechanisms of fracture; ductile tearing dimples;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The paper describes the main regularities of plastic deformation in VT22 titanium alloy and the micromechanisms of its fracture in static tension and in tension after different dynamic nonequilibrium loading modes resulting from the application of additional pulse loads. It is found that irrespective of the result of loading, the fracture of alloy VT22 occurs by the pore nucleation and coalescence mechanism. The physico-mechanical phenomena underlying the formation of ductile tearing dimples on fracture surfaces are analyzed and their relation to the deformation processes is described.
引用
收藏
页码：436 / 445
页数：9
相关论文
共 50 条
  • [31] The Influence of Surface Hardening by Combined Thermo-Forced Impacts on the Fatigue Life and Damage of the VT22 Titanium Alloy
    Bagmutov, V. P.
    Vodop'yanov, V. I.
    Zakharov, I. N.
    Denisevich, D. S.
    Romanenko, M. D.
    Nazarov, N. G.
    RUSSIAN JOURNAL OF NON-FERROUS METALS, 2021, 62 (01) : 64 - 71
  • [32] The Influence of Surface Hardening by Combined Thermo-Forced Impacts on the Fatigue Life and Damage of the VT22 Titanium Alloy
    V. P. Bagmutov
    V. I. Vodop’yanov
    I. N. Zakharov
    D. S. Denisevich
    M. D. Romanenko
    N. G. Nazarov
    Russian Journal of Non-Ferrous Metals, 2021, 62 : 64 - 71
  • [33] Effect of high-temperature loading on dislocation slip and structural rearrangements in a titanium alloy VT22 subjected to small deformations
    Mazurskii, MI
    Enikeev, FU
    Vasin, RA
    Muravlev, AV
    Chistyakov, PV
    Karavaeva, MV
    FIZIKA METALLOV I METALLOVEDENIE, 1999, 88 (05): : 90 - 94
  • [34] CHANGE IN ALLOY ELEMENT AND IMPURITY CONTENT ON THE FRACTURE SURFACE OF VT22 ALLOY SPECIMENS WITH DIFFERENT STRUCTURES
    POLKIN, IS
    ISHUNKINA, TV
    REDKIN, VS
    CHASNIKOV, AI
    TKACHENKO, EA
    METAL SCIENCE AND HEAT TREATMENT, 1991, 33 (11-12) : 932 - 934
  • [35] STRUCTURE AND PROPERTIES OF VT22 ALLOY AFTER THERMAL CYCLING TREATMENT AND ANNEALING
    LYASOTSKAYA, VS
    LYASOTSKII, IV
    FEOKTISTOVA, EK
    MALEEVA, NV
    METAL SCIENCE AND HEAT TREATMENT, 1983, 25 (11-1) : 864 - 868
  • [36] FRACTURE TYPE OF VT16 AND VT22 HIGH-TENSILE TITANIUM-ALLOYS WITH DIFFERENT STRUCTURES
    POLKIN, IS
    RODIONOV, VL
    ISHUNKINA, TV
    KUDRYASHOV, VG
    INDUSTRIAL LABORATORY, 1983, 49 (11): : 1182 - 1185
  • [37] Effect of electrolyte depletion on the characteristics of the anodic plasma electrolytic nitriding of a VT22 titanium alloy
    Smirnov A.A.
    Kusmanov S.A.
    Kusmanova I.A.
    Belkin P.N.
    Surface Engineering and Applied Electrochemistry, 2017, 53 (5) : 413 - 418
  • [38] Plasma electrolytic treatment of VT22 titanium alloy in electrolytes with carbon-containing compounds
    Kusmanov S.A.
    Dyakov I.G.
    Belkin P.N.
    Parfenyuk V.I.
    Surface Engineering and Applied Electrochemistry, 2017, 53 (1) : 1 - 6
  • [39] Anodic plasma electrolytic nitrocarburising of VT22 titanium alloy in carbamide and ammonium chloride electrolyte
    Tambovskiy I.V.
    Kusmanov S.A.
    Korableva S.S.
    Silkin S.A.
    Sevostyanov N.V.
    Komissarova M.R.
    Belkin P.N.
    Surface Engineering and Applied Electrochemistry, 2017, 53 (5) : 407 - 412
  • [40] Influence of Annealing on the Structure and Mechanical Properties of Ultrafine-Grained VT22 Titanium Alloy
    I. V. Ratochka
    E. V. Naydenkin
    O. N. Lykova
    I. P. Mishin
    Russian Physics Journal, 2019, 62 : 1322 - 1329
12345