Resistance of Plate Shipbuilding Steels to Cavitation-Erosion and Fatigue Fracture

被引：0
|
作者：
O. I. Balyts’kyi
J. Chmiel
机构：
[1] Ukrainian National Academy of Sciences,Karpenko Physicomechanical Institute
[2] Maritime Academy,undefined
来源：
Materials Science | 2015年 / 50卷
关键词：
cavitation fracture; low-cycle fatigue; shipbuilding steel; in-service degradation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We recommend to use SSAB Domex steel microalloyed with boron and characterized by elevated resistances to corrosion-erosion fracture and low-cycle fatigue instead of the widespread 18Mn2 steel in the water transport and elements of hydroengineering structures subjected to the action of strong water flows including, in particular, the Kort nozzles, rudder drives, and parts of the river-ship hulls especially sensitive to erosion.
引用
收藏
页码：736 / 739
页数：3
相关论文
共 50 条
  • [31] Cavitation-erosion resistance of arc ion-plated (Ti,Cr)N coatings
    Pan, GS
    Yang, WY
    [J]. SCIENCE IN CHINA SERIES A-MATHEMATICS, 2001, 44 : 369 - 374
  • [32] CAVITATION-EROSION FAILURE OF CAST-IRON COMPONENTS
    ABRAMENKO, YE
    ABRAMENKO, VY
    [J]. METAL SCIENCE AND HEAT TREATMENT, 1989, 31 (3-4) : 258 - 262
  • [33] Effects of Plasma Ion Nitriding Temperatures on Cavitation-Erosion Resistance of STS 304 in Seawater
    Chong, S. O.
    Kim, S. J.
    [J]. ACTA PHYSICA POLONICA A, 2019, 135 (05) : 968 - 971
  • [34] DAMAGE OF MICROPATTERNED SURFACES DUE TO BUBBLE CAVITATION-EROSION
    Jee, T.
    Komvopoulos, K.
    [J]. PROCEEDINGS OF THE STLE/ASME INTERNATIONAL JOINT TRIBOLOGY CONFERENCE, 2010, 2011, : 33 - 35
  • [35] Cavitation-erosion in mercury spallation neutron target source
    Haines, JR
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2005, 343 (1-3) : 366 - 366
  • [36] Cavitation-Erosion Wear of Aminoplast in Simulated Environments of Sugar Production
    Martynyuk, A. V.
    Stechyshyn, M. S.
    Tsepenyuk, M. I.
    Boris, M. M.
    Bandura, V. M.
    Mikhalevskiy, V. Ts.
    [J]. MATERIALS SCIENCE, 2024, 59 (06) : 673 - 678
  • [37] Preliminary evaluation of cavitation-erosion resistance of Ti-alloys in mercury for the Spallation Neutron Source
    Pawel, S. J.
    Mansur, L. K.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2010, 398 (1-3) : 180 - 188
  • [38] Investigation on Cavitation-Erosion Damage with the Cavitation Amplitude of Al Alloy Materials in Seawater
    Yang, Ye-Jin
    Kim, Seong-Jong
    [J]. CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2020, 19 (05): : 250 - 258
  • [39] Correlation between cavitation erosion and random fatigue properties of selected steels
    Bedkowski, W
    Gasiak, G
    Lichtarowicz, A
    Macha, E
    [J]. ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1325 - 1330
  • [40] Cavitation-erosion resistance of 316LN stainless steel in mercury containing metallic solutes
    Pawel, S. J.
    Mansur, L. K.
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2008, 377 (01) : 174 - 181
12345