Effect of Carbon and Manganese on Low-Carbon Pipe Steel Hydrogen-Induced Cracking Resistance

被引：0
|
作者：
A. A. Kholodnyi
Yu. I. Matrosov
M. Yu. Matrosov
S. V. Sosin
机构：
[1] Bardin Central Research Institute of Ferrous Metallurgy (TsNIIchermet),
[2] Azovstal Metallurgical Combine,undefined
[3] Metinvest Group,undefined
来源：
Metallurgist | 2016年 / 60卷
关键词：
low-carbon pipe steel; continuously-cast slab; thick rolled sheet; chemical composition; thermomechanical treatment; hardness; hydrogen-induced cracking (HIC);
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A favorable effect is established for reducing carbon and manganese content in low-alloy pipe steels of strength categories X56–X65 on the increase in hydrogen-induced cracking (HIC) resistance of thick-rolled sheet prepared by a thermomechanical treatment regime. This effect is due to a reduction in segregation structural inhomogeneity in the axial area of sheets in the form of a solid band of high-carbon structures.
引用
收藏
页码：54 / 60
页数：6
相关论文
共 50 条
  • [41] Effect of silicon and manganese on mechanical properties of low-carbon plain TRIP steel
    Li, Z
    Wu, D
    Hu, R
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2005, 12 (03) : 51 - 55
  • [42] Effect of strain rate on hydrogen embrittlement in low-carbon martensitic steel
    Momotani, Yuji
    Shibata, Alzinobu
    Terada, Daisuke
    Tsuji, Nobuhiro
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2017, 42 (05) : 3371 - 3379
  • [43] PREVENTION OF SOLIDIFICATION CRACKING IN VERY LOW-CARBON STEEL WELDS
    OHSHITA, S
    YURIOKA, N
    MORI, N
    KIMURA, T
    WELDING JOURNAL, 1983, 62 (05) : S129 - S136
  • [44] Effect of boron on the microstructure of low-carbon steel resistance seam welds
    Babu, SS
    Goodwin, GM
    Rohde, RJ
    Sielen, B
    WELDING JOURNAL, 1998, 77 (06) : 249S - 253S
  • [45] Effect of boron on the microstructure of low-carbon steel resistance seam welds
    Oak Ridge Natl Lab, Oak Ridge, United States
    Weld J (Miami Fla), 6 (249s-253s):
  • [46] Effect of Nb on the hydrogen-induced cracking of high-strength low-alloy steel
    Zhang Shiqi
    Fan Endian
    Wan Jifang
    Liu Jing
    Huang Yunhua
    Li Xiaogang
    CORROSION SCIENCE, 2018, 139 : 83 - 96
  • [47] Suppression of hydrogen-induced damage in friction stir welded low carbon steel joints
    Sun, Yufeng
    Fujii, Hidetoshi
    Imai, Hisashi
    Kondoh, Katsuyoshi
    CORROSION SCIENCE, 2015, 94 : 88 - 98
  • [48] EFFECT OF TEMPERATURE AND STRAIN RATE ON CLEAVAGE FRACTURE IN A MILD STEEL AND A LOW-CARBON MANGANESE STEEL
    OATES, G
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1969, 207 : 353 - &
  • [49] THE EFFECT OF MANGANESE CONTENT IN STEEL AND SLAB HEAT TEMPERATURE ON THE PHOSPHATABILITY OF ULTRA LOW-CARBON STEEL
    KAJIWARA, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05): : S460 - S460
  • [50] EFFECT OF CU ON HYDROGEN INDUCED CRACKING OF PIPE LINE STEEL
    INAGAKI, H
    TANIMURA, M
    MATSUSHIMA, I
    NISHIMURA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1978, 18 (03) : 149 - 156
12345