Updating the Mode of Annealing of Tubes from Steel ShKh15 in Chamber Furnaces

被引：0
|
作者：
B. P. Yur’ev
V. A. Gol’tsev
机构：
[1] Ural Federal University after the First President of Russia B. N. Eltsyn,
来源：
Metal Science and Heat Treatment | 2016年 / 58卷
关键词：
chamber furnace; annealing mode; steel ShKh15; tubes; charge; heat treatment process; strength; microstructure; rejection; output;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A study of commercial tubes from steel ShKh15 produced in a chamber furnace is performed for investigating the active annealing process. The causes of inappropriate heating and cooling of tubes in a charge are determined. The annealing mode is shown to mismatch the required temperature regime, which elevates rejection. Recommendations for eliminating the determined drawbacks, raising the quality of the annealed tubes and the output of the chamber furnaces are developed.
引用
收藏
页码：421 / 425
页数：4
相关论文
共 50 条
  • [21] DECOMPOSITION OF MARTENSITE IN STEEL SHKH15 IN THE PROCESS OF QUENCHING
    KAGAN, AS
    SPEKTOR, AG
    TSILMAN, RI
    METAL SCIENCE AND HEAT TREATMENT, 1981, 23 (9-10) : 691 - 693
  • [22] DEVELOPING A NEW HOMOGENIZING (DIFFUSION ANNEALING) PRACTICE FOR SHKH15 BALL-BEARING STEEL
    CHERNYAVSKAYA, SG
    MALINOVS.TI
    MOSHKEVI.LD
    KHITRIK, AI
    TRAVININ, VI
    STETSENK.NA
    STAL IN ENGLISH-USSR, 1967, (09): : 786 - +
  • [23] STABILITY OF SURFACE-LAYER OF BEARING STEEL SHKH15
    RANKOVA, AG
    KORTOV, VS
    KHENKIN, ML
    GAPRINDASHVILI, AI
    GUSEVA, GM
    METAL SCIENCE AND HEAT TREATMENT, 1975, 17 (5-6) : 532 - 534
  • [24] Deformability of ShKh15 Steel during Cold Plastic Deformation
    Blinov, V. M.
    Doronin, I. V.
    Antoschenkov, A. E.
    Lukina, Yu. A.
    RUSSIAN METALLURGY, 2007, 2007 (02): : 140 - 142
  • [25] MAGNETIC INSPECTION OF THE HARDNESS OF STEEL ShKh15 PIPES.
    Konovalov, O.S.
    Brusentsova, R.M.
    Tovpinets, A.A.
    Roitman, V.I.
    The Soviet journal of nondestructive testing, 1982, 18 (12): : 999 - 1000
  • [26] Residual durability of the surface layer of ShKh15 bearing steel
    Datsyshyn, OP
    Marchenko, HP
    Zynyuk, OD
    Hrytsyshyn, PM
    MATERIALS SCIENCE, 1995, 31 (02) : 192 - 199
  • [27] CONTACT FATIGUE-STRENGTH OF POWDER STEEL SHKH15
    ABASHKINA, NV
    REPINA, AI
    IVANOV, VS
    POPOV, OA
    METAL SCIENCE AND HEAT TREATMENT, 1990, 32 (7-8) : 623 - 626
  • [28] COMMISSIONING A NEW ROLLER-HEARTH TUNNEL FURNACE FOR HEAT TREATMENT OF TUBES OF STEEL SHKH15
    STANTSEL, IP
    RUKAVISH.SA
    STAL IN ENGLISH-USSR, 1966, (10): : 848 - &
  • [29] PREPARATION AND PROPERTIES OF P/M SHKH15 STEEL FROM MACHINING WASTE
    NARVA, VK
    LOSHKAREVA, NS
    PAVLOV, SA
    BATASHEV, KV
    SOVIET POWDER METALLURGY AND METAL CERAMICS, 1988, 27 (08): : 609 - 611
  • [30] SIZED GRADE SHKH15 STEEL GROUND IN AUTOMATIC MACHINES
    ANTIPOV, KI
    FURSOV, BT
    STAL IN ENGLISH-USSR, 1968, (12): : 1060 - +
12345