Conditions for the Transition from Nonlocalized to Localized Damage in Metals and Alloys. Part 1. Crack Sizes at Fatigue Limit

被引：0

作者：

V. T. Troshchenko

L. A. Khamaza

机构：

[1] National Academy of Sciences of Ukraine,Pisarenko Institute of Problems of Strength

来源：

Strength of Materials | 2014年 / 46卷

关键词：

fatigue limit; nonpropagating fatigue cracks; fracture mechanics;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The paper addresses special features of nonlocalized and localized fatigue damage in metals and alloys. The sizes of maximum fatigue cracks at a fatigue limit in metals and alloys of various grain sizes and strengths are analyzed. The authors discuss the linear and nonlinear fracture mechanics criteria that relate the fatigue crack sizes and the fatigue limits. The experimental values of the fatigue crack size are compared to those calculated by different criteria. Special features of initiation of nonpropagating fatigue cracks in the presence of stress concentrators are studied.

引用

页码：303 / 314

页数：11

共 27 条

[21] Experimental Mold for Producing Concast Billets from High-Alloyed Steels and Alloys. Part 1. Preliminary Thermal Testing and Design of the Mold
V. V. Stulov
O. M. Shafiev
Metallurgist, 2023, 66 : 1192 - 1200
[22] Fatigue crack growth from foreign object damage under combined low and high cycle loading. Part 1: Experimental studies
Ding, J.
Hall, R. F.
Byrne, J.
Tong, J.
INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (07) : 1339 - 1349
[23] Prospective Refractory Materials For Smelting and Sintering Alloys Based on Titanium and Other Transition Metals. Part 1. Calcium Zirconate Synthesis for Ceramic Products
B. L. Krasniy
K. I. Ikonnikov
A. L. Galganova
O. I. Rodinov
Refractories and Industrial Ceramics, 2022, 63 : 55 - 59
[24] Prospective Refractory Materials For Smelting and Sintering Alloys Based on Titanium and Other Transition Metals. Part 1. Calcium Zirconate Synthesis for Ceramic Products
Krasniy, B. L.
Ikonnikov, K. I.
Galganova, A. L.
Rodinov, O., I
REFRACTORIES AND INDUSTRIAL CERAMICS, 2022, 63 (01) : 55 - 59
[25] Prediction of gigacycle fatigue resistance characteristics of metals from high-frequency test data. Part 1. Experimental results
Matokhnyuk, L. E.
Yakovleva, T. Yu
Byalonovich, A. V.
STRENGTH OF MATERIALS, 2012, 44 (04) : 395 - 403
[26] Prediction of gigacycle fatigue resistance characteristics of metals from high-frequency test data. Part 1. Experimental results
L. E. Matokhnyuk
T. Yu. Yakovleva
A. V. Byalonovich
Strength of Materials, 2012, 44 : 395 - 403
[27] Resistance spot welding of aluminum alloy to steel with transition material - From process to performance - Part 1: Experimental study - Weld strength, failure mode, and fatigue life were compared with self-piercing rivets of the same dissimilar metals combination
Sun, X
Stephens, EV
Khaleel, MA
Shao, H
Kimchi, M
WELDING JOURNAL, 2004, 83 (06) : 188S - 195S

← 1 2 3 →