Moisture ingression in honeycomb core sandwich panels

被引：0
|
作者：
D. Cise
R. S. Lakes
机构：
[1] University of Iowa,Department of Biomedical Engineering, Department of Mechanical Engineering, Center for Laser Science and Engineering, 238 IATL
来源：
Journal of Materials Engineering and Performance | 1997年 / 6卷
关键词：
core; honeycomb panels; moisture; sandwich panel; water;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Moisture ingression was studied in several composite sandwich panels, in which hydration was applied over a large surface area at the panel edges. Significant moisture ingression occurred in panels with cores of Korex (based on a substrate of a fiber pulp paper) and HRP (consisting of a woven-glass-fiber substrate with a polymer coating) of different density. Ingression was more rapid than in panels with hydration applied locally. Ingression followed an exponential pattern in time in most cases, in harmony with diffusion theory.
引用
收藏
页码：732 / 736
页数：4
相关论文
共 50 条
  • [41] THERMOCHEMICAL RESPONSE OF HONEYCOMB SANDWICH PANELS
    RAMOHALLI, K
    JOURNAL OF FIRE SCIENCES, 1983, 1 (05) : 379 - 395
  • [42] ADHESIVE-FREE THERMOPLASTIC SANDWICH PANELS Bonding of Adhesive-Free Thermoplastic Sandwich Panels with Honeycomb Core for Aircraft Interiors
    Latsuzbayall, Temuri
    Middendorf, Peter
    Voelkle, Dietmar
    Weber, Christoph
    SAMPE JOURNAL, 2022, 58 (02) : 38 - 43
  • [43] A COMPARISON OF HONEYCOMB-CORE AND FOAM-CORE CARBON-FIBER EPOXY SANDWICH PANELS
    AKAY, M
    HANNA, R
    COMPOSITES, 1990, 21 (04): : 325 - 331
  • [44] Vibration and aeroelastic stability analysis of hexagonal honeycomb core sandwich panels in supersonic airflow
    Jian, Zhou
    Xu, Minglong
    Zhang, Zhijia
    Zheng, Tian
    THIN-WALLED STRUCTURES, 2022, 180
  • [45] The Response of Honeycomb Core Sandwich Panels, with Aluminum and Composite Face Sheets, to Blast Loading
    Langdon, G. S.
    Nurick, G. N.
    Yahya, M. Yazid
    Cantwell, W. J.
    JOURNAL OF SANDWICH STRUCTURES & MATERIALS, 2010, 12 (06) : 733 - 754
  • [46] Compression After Impact Experiments on Thin Face Sheet Honeycomb Core Sandwich Panels
    McQuigg, Thomas D.
    Kapania, Rakesh K.
    Scotti, Stephen J.
    Walker, Sandra P.
    JOURNAL OF SPACECRAFT AND ROCKETS, 2014, 51 (01) : 253 - 266
  • [47] Tensile characterization of composite honeycomb core sandwich panels after low velocity impact
    Kou, Changhe
    Cheng, Xiaoquan
    Li, Zhengneng
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 15 (04): : 69 - 73
  • [48] Anti-Explosion Analysis of Honeycomb Sandwich Panels with Three Kinds of Core Structures
    Zhang H.
    Chang B.
    Zhao K.
    Zheng Z.
    Yu J.
    Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology, 2022, 42 (06): : 557 - 566
  • [49] Stability and Failure of the Edge-Closed Honeycomb Sandwich Panels with Face/Core Debonding
    Yan, Bing
    Wang, Xinfeng
    Pan, Song
    Tong, Mingbo
    Yu, Jian
    Liu, Fan
    APPLIED SCIENCES-BASEL, 2020, 10 (21): : 1 - 19
  • [50] Study on damage of composite honeycomb core sandwich panels under low velocity impact
    Beijing Univ of Aeronautics &, Astronautics, Beijing, China
    Fuhe Cailiao Xuebao, 3 (124-128):
12345