Preparation and degradation characteristics of poly (d, l-lactide) composite films

被引：0
|
作者：
Lei Chen
Yuhua Yan
Jianhua Li
Shipu Li
机构：
[1] Wuhan University of Technology,Biomedical Materials and Engineering Research Center
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2007年 / 22卷
关键词：
poly (d, l-lactic acid) (PDLLA); chitosan (CHI); -TCP; nerve growth factor (NGF); degradation characteristics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
PDLLA/CHI/β-TCP/NGF composite films were prepared by a solvent evaporation method. The degradation characteristics of the poly (d, l-lactide) composite films were studied in vitro and in vivo. The acidity produced by poly (d, l-lactide) materials was not obvious. Adding chitosan and β-TCP can relieve the acidity problem and improve strength performance of films. The NGF has influences on the degradation characteristics of films. It is verified that PDLLA/CHI/β-TCP/NGF composite films prepared by solvent evaporation method have excellent degradation characteristics. It can be used as a perfect biomaterial for repairing nerve injuries.
引用
下载
收藏
相关论文
共 50 条
  • [31] Poly(L-lactide) degradation by Saccharothrix waywayandensis
    Jarerat, A
    Tokiwa, Y
    BIOTECHNOLOGY LETTERS, 2003, 25 (05) : 401 - 404
  • [32] In vitro stability of poly(D,L-lactide) and poly(D,L-lactide)/poloxamer nanoparticles in gastrointestinal fluids
    Reich, G
    DRUG DEVELOPMENT AND INDUSTRIAL PHARMACY, 1997, 23 (12) : 1191 - 1200
  • [33] Hydrolytic degradation of amorphous films of L-lactide copolymers with glycolide and D-lactide
    Saha, SK
    Tsuji, H
    MACROMOLECULAR MATERIALS AND ENGINEERING, 2006, 291 (04) : 357 - 368
  • [34] Radiation-induced degradation of hydroxyapatite/poly L-lactide composite biomaterial
    Suljovrujic, E.
    Ignjatovic, N.
    Uskokovic, D.
    Mitric, M.
    Mitrovic, M.
    Tomic, S.
    RADIATION PHYSICS AND CHEMISTRY, 2007, 76 (04) : 722 - 728
  • [35] Preparation, characterization and biodegradation characteristics of poly(adipic anhydride-co-D,L-lactide)
    Zhu, KJ
    Lei, YA
    POLYMER INTERNATIONAL, 1997, 43 (03) : 210 - 216
  • [36] In vitro degradation behavior of β-calcium metaphosphate whiskers/poly L-lactide composite
    Chen, Lin
    Liao, Li
    Kang, Yunqing
    Yin, Guangfu
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2007, 24 (06): : 100 - 104
  • [37] Preparation and characterization of poly(D,L-lactide) and its porous biomaterials
    Zhong-cheng Zhou
    Jian-ming Ruan
    Bai-yun Huang
    Ya-jun Li
    Jian-peng Zou
    Hai-bo Zhang
    Journal of Central South University of Technology, 2005, 12 : 1 - 4
  • [38] Preparation and characterization of poly(D,L-lactide) and its porous biomaterials
    Zhou, ZC
    Ruan, JM
    Huang, BY
    Li, YJ
    Zou, JP
    Zhang, HB
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2005, 12 (01): : 1 - 4
  • [39] Piezoelectricity of Poly(L-lactic Acid) Composite Film with Stereocomplex of Poly(L-lactide) and Poly(D-lactide)
    Yoshida, Tetsuo
    Imoto, Kenji
    Tahara, Komei
    Naka, Kyohei
    Uehara, Yusuke
    Kataoka, Shingo
    Date, Munehiro
    Fukada, Eiichi
    Tajitsu, Yoshiro
    JAPANESE JOURNAL OF APPLIED PHYSICS, 2010, 49 (09)
  • [40] Preparation and characterization of poly(D,L-lactide) and its porous biomaterials
    周忠诚
    阮建明
    黄伯云
    李亚军
    邹俭鹏
    张海波
    Journal of Central South University, 2005, (01) : 1 - 4
12345