Preparation and degradation characteristics of poly (d, l-lactide) composite films

被引：0
|
作者：
Lei Chen
Yuhua Yan
Jianhua Li
Shipu Li
机构：
[1] Wuhan University of Technology,Biomedical Materials and Engineering Research Center
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2007年 / 22卷
关键词：
poly (d, l-lactic acid) (PDLLA); chitosan (CHI); -TCP; nerve growth factor (NGF); degradation characteristics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
PDLLA/CHI/β-TCP/NGF composite films were prepared by a solvent evaporation method. The degradation characteristics of the poly (d, l-lactide) composite films were studied in vitro and in vivo. The acidity produced by poly (d, l-lactide) materials was not obvious. Adding chitosan and β-TCP can relieve the acidity problem and improve strength performance of films. The NGF has influences on the degradation characteristics of films. It is verified that PDLLA/CHI/β-TCP/NGF composite films prepared by solvent evaporation method have excellent degradation characteristics. It can be used as a perfect biomaterial for repairing nerve injuries.
引用
收藏
相关论文
共 50 条
  • [1] Preparation and degradation characteristics of poly (d, l-lactide) composite films
    Chen Lei
    Yan Yuhua
    Li Jianhua
    Li Shipu
    [J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2007, 22 (04): : 691 - 694
  • [2] Preparation and characterization of pentapeptide-grafted poly(D,L-lactide)/nanohydroxyapatite/poly(D,L-lactide) composite membrane
    Yingying Ban
    Youfa Wang
    [J]. Polymer Science Series B, 2015, 57 : 530 - 537
  • [3] Preparation and characterization of pentapeptide-grafted poly(D,L-lactide)/nanohydroxyapatite/poly(D,L-lactide) composite membrane
    Ban, Yingying
    Wang, Youfa
    [J]. POLYMER SCIENCE SERIES B, 2015, 57 (05) : 530 - 537
  • [4] l-Lactide Additive and in Vitro Degradation Performance of Poly(l-lactide) Films
    Mobedi, Hamid
    Mashak, Arezou
    Nekoomanesh, Mehdi
    Orafai, Hossein
    [J]. IRANIAN POLYMER JOURNAL, 2011, 20 (03) : 237 - 245
  • [5] Preparation of nano-hydroxyapatite/poly(D,L-lactide) composite and its degradation in femora of rabbits
    Xiao, YM
    Fan, HS
    Wang, XL
    Xu, JR
    Cheng, JQ
    Li, XD
    Zhang, XD
    [J]. ASBM6: ADVANCED BIOMATERIALS VI, 2005, 288-289 : 203 - 206
  • [6] Degradation of poly (L-lactide).
    Albertsson, AC
    Khabbaz, F
    Hakkarainen, M
    [J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2001, 221 : U355 - U355
  • [7] Preparation and characterization of poly(L-lactide)/poly(ε-caprolactone) composite films for food packaging application
    Yang, Ji-Yi
    Qin, Yu-Yue
    Cao, Jian-Xin
    Yuan, Ming-Wei
    Liu, Shi-Qi
    Yuan, Ming-Long
    [J]. ADVANCED ENGINEERING MATERIALS III, PTS 1-3, 2013, 750-752 : 845 - +
  • [8] Alkaline and enzymatic degradation of L-lactide copolymers.: II.: Crystallized films of poly(L-lactide-co-D-lactide) and poly(L-lactide) with similar crystallinities
    Tsuji, H
    Tezuka, Y
    Yamada, K
    [J]. JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 2005, 43 (09) : 1064 - 1075
  • [9] Preparation of Chitosan/Poly(L-Lactide) Porous Composite Scaffolds
    CHEN Pin1
    [J]. Chinese Journal of Biomedical Engineering, 2012, 21 (02) : 67 - 72
  • [10] Preparation and degradation of L-lactide and ε-caprolactone homo and copolymer films
    Yavuz, H
    Babaç, C
    Tuzlakoglu, K
    Piskin, E
    [J]. POLYMER DEGRADATION AND STABILITY, 2002, 75 (03) : 431 - 437
12345