Study of aluminum hydroxide powder prepared by chemical dispersion of aluminum and its alloy

被引：0
|
作者：
A. D. Shlyapin
A. Yu. Omarov
A. Kh. Khairi
Yu. G. Trifonov
机构：
[1] FGBOU VPO Moscow State Industrial University,
来源：
Refractories and Industrial Ceramics | 2013年 / 53卷
关键词：
hydrogen generator; aluminum hydroxide; chemical dispersion; aluminum; silumin; gibbsite; bayerite; powder dispersed composition; reaction kinetics; powder preparation methods;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Aluminum hydroxide is a secondary product during operation of a hydrogen generator. An alkaline reaction proceeding between aluminum or aluminum alloy and caustic soda may be considered as a chemical dispersion method with preparation of nanodispersed aluminum hydroxide powder. Particle fineness and morphology, and also aluminum hydroxide powder phase composition, are different with different preparation methods, and therefore x-ray-phase, petrographic, and dimensional analyses are performed for three powder samples. Two powder samples are studied, prepared by chemical dispersion of aluminum (sample 1) and silumin AK7 (sample 2). Results for industrially produced aluminum hydroxide powder, prepared by the Bayer method (sample 3) are studied for comparison.
引用
收藏
页码：317 / 321
页数：4
相关论文
共 50 条
  • [31] Comparative Study on Combustion Behavior of Aluminum-Based Alloy Fuels and Aluminum Powder in Solid Propellants
    Xin, Haoyue
    Wang, Kun
    Ren, Hui
    Jiao, Qingjie
    METALS, 2023, 13 (08)
  • [32] Porous Permeable Corundum Ceramic Based on Aluminum Powder. Part 1. Study of Different Grades of Aluminum Hydroxide Powder Properties
    Krasnyi, B. L.
    Tarasovskii, V. P.
    Mosin, Yu. M.
    Krasnyi, A. B.
    Omarov, A. Yu.
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2014, 55 (01) : 30 - 35
  • [33] Investigation of the Structure and Phase Composition of Aluminum Oxide Powders Obtained by Chemical Dispersion of an Aluminum Alloy with Different Magnesium Content
    A. D. Shlyapin
    V. P. Tarasovskii
    A. Yu. Omarov
    V. S. Nikol’skii
    I. A. Kurbatova
    Glass and Ceramics, 2014, 70 : 437 - 440
  • [34] Investigation of the Structure and Phase Composition of Aluminum Oxide Powders Obtained by Chemical Dispersion of an Aluminum Alloy with Different Magnesium Content
    Shlyapin, A. D.
    Tarasovskii, V. P.
    Omarov, A. Yu.
    Nikol'skii, V. S.
    Kurbatova, I. A.
    GLASS AND CERAMICS, 2014, 70 (11-12) : 437 - 440
  • [35] ULTRAFINE ALUMINUM-OXIDE POWDER PREPARED BY CHEMICAL VAPOR-DEPOSITION OF TRIMETHYLALUMINUM
    KIM, KH
    HO, CH
    SUH, TG
    PRAKASH, S
    BUNSHAH, RF
    JOURNAL OF MATERIALS ENGINEERING, 1991, 13 (03) : 199 - 205
  • [36] Effect of process parameters on synthesis of aluminum nitride powder prepared by chemical vapor deposition
    Moo-Chin Wang
    Ming-Sung Tsai
    Nan-Chung Wu
    Journal of Materials Science, 2001, 36 : 3283 - 3289
  • [37] Comparative Study on the Failure of Adhesively Bonded GFRP/Aluminum Alloy and Aluminum Alloy/Aluminum Alloy Joints
    Qin G.
    Na J.
    Mu W.
    Tan W.
    Liu H.
    Qiche Gongcheng/Automotive Engineering, 2019, 41 (05): : 599 - 606
  • [38] Effect of process parameters on synthesis of aluminum nitride powder prepared by chemical vapor deposition
    Wang, MC
    Tsai, MS
    Wu, NC
    JOURNAL OF MATERIALS SCIENCE, 2001, 36 (13) : 3283 - 3289
  • [39] Structure and phase composition of the powder prepared by chemical dispersion of aluminium-vanadium alloy
    Omarov, A. Yu.
    Nikishkina, O. V.
    Shlyapin, A. D.
    INTERNATIONAL JOURNAL OF ADVANCED BIOTECHNOLOGY AND RESEARCH, 2016, 7 (04): : 1381 - 1385
  • [40] Powder-forged aluminum alloy scroll
    Sumitomo Electric Technical Review, 1993, (35):
12345