Hot Corrosion Behavior of Si–Y–Co-Modified Aluminide Coating Exposed to NaCl + Na2SO4 Salt at 1173 K

被引：1
|
作者：
Zongjie Liu
Chungen Zhou
机构：
[1] Beijing University of Aeronautics and Astronautics,Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering
来源：
Oxidation of Metals | 2016年 / 85卷
关键词：
Metal coatings; Superalloys; Hot corrosion;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：205 / 217
页数：12
相关论文
共 50 条
  • [21] DTA STUDIES ON THE CORROSION BEHAVIOR OF TITANIUM POWDER IN NACL AND NA2SO4
    KAMESWARI, S
    JOURNAL OF THERMAL ANALYSIS, 1990, 36 (01): : 23 - 33
  • [22] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050 °C
    Hongyu Wang
    Han Wang
    Peng Kan
    Qian Zhao
    Xiang Zhang
    Yang Ding
    Oxidation of Metals, 2018, 90 : 571 - 583
  • [23] Hot Corrosion Behavior of Ce-Modified NiAl Coating by Cl-Containing Na2SO4 at 1050°C
    Wang, Hongyu
    Wang, Han
    Kan, Peng
    Zhao, Qian
    Zhang, Xiang
    Ding, Yang
    OXIDATION OF METALS, 2018, 90 (5-6): : 571 - 583
  • [24] E-PO2-DIAGRAM FOR NICKEL CORROSION IN NA2SO4 AT 1173-K
    SEQUEIRA, CAC
    HOCKING, MG
    BRITISH CORROSION JOURNAL, 1977, 12 (03): : 158 - 162
  • [25] HOT CORROSION OF COCRALY TURBINE BLADE COATINGS BY NA2SO4 AND VAPOROUS NACL
    JONES, RL
    GADOMSKI, ST
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1977, 124 (10) : 1641 - 1648
  • [26] Comparison investigation of hot corrosion exposed to Na2SO4 salt and oxidation of MoSi2-based coating on Nb alloy at 1000 °C
    Sun, Le
    Fu, Qian-Gang
    Sun, Jia
    Zhang, Guang-peng
    SURFACE & COATINGS TECHNOLOGY, 2020, 385 (385):
  • [27] Microstructure and hot corrosion behavior of Co-Si modified aluminide coating on nickel based superalloys
    He, Haiyan
    Liu, Zongjie
    Wang, Wan
    Zhou, Chungen
    CORROSION SCIENCE, 2015, 100 : 466 - 473
  • [28] Hot Corrosion Behavior of ZrB2-SiC-Graphite Composite in NaCl and Na2SO4 Molten Salts
    Liu, X.
    Wang, G.
    Liu, L.
    Wang, Z.
    Wu, Z.
    Liu, M.
    JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2018, 9 (03): : 309 - 317
  • [29] Study of hot corrosion resistance of electroless nickel coating with different content of phosphorous in molten salt deposit Na2SO4–NaCl at 650°C
    Ghaderi M.
    Rezagholizadeh M.
    Nasiri-Vatan H.
    Ebrahimi-Kahrizsangi R.
    Surface Engineering and Applied Electrochemistry, 2015, 51 (04) : 367 - 373
  • [30] Kinetics and mechanism of hot corrosion of γ-Y2Si2O7 in thin-film Na2SO4 molten salt
    Sun, Ziqi
    Li, Meishuan
    Zhou, Yanchun
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2008, 91 (07) : 2236 - 2242
12345