Hot Corrosion Behavior of Si–Y–Co-Modified Aluminide Coating Exposed to NaCl + Na2SO4 Salt at 1173 K

被引：1
|
作者：
Zongjie Liu
Chungen Zhou
机构：
[1] Beijing University of Aeronautics and Astronautics,Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering
来源：
Oxidation of Metals | 2016年 / 85卷
关键词：
Metal coatings; Superalloys; Hot corrosion;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：205 / 217
页数：12
相关论文
共 50 条
  • [1] Hot Corrosion Behavior of Si-Y-Co-Modified Aluminide Coating Exposed to NaCl + Na2SO4 Salt at 1173 K
    Liu, Zongjie
    Zhou, Chungen
    OXIDATION OF METALS, 2016, 85 (1-2): : 205 - 217
  • [2] Hot Corrosion of Co-based Alloys with 25%NaCl+75%Na2SO4 Coating at 1173 K
    Fu, Guangyan
    Guo, Xingxing
    Liu, Qun
    Zhao, Xin
    Su, Yong
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2013, 32 (03) : 317 - 321
  • [3] Role of iridium in hot corrosion resistance of pt-ir modified aluminide coatings with Na2SO4-NaCl salt at 1173 K
    Wu, Ying-Na
    Yamaguchi, Akihiro
    Murakami, Hideyuki
    Kuroda, Seiji
    MATERIALS TRANSACTIONS, 2006, 47 (08) : 1918 - 1921
  • [4] Hot corrosion behavior of Pt plus Hf co-modified NiAl coating in the mixed salt of Na2SO4-NaCl at 900 °C
    Yang, Y. F.
    Liu, Z. L.
    Ren, P.
    Wang, Q. W.
    Bao, Z. B.
    Zhu, S. L.
    Li, W.
    CORROSION SCIENCE, 2020, 167
  • [5] HOT CORROSION BEHAVIOR OF NIMONIC-105 IN NACL AND NA2SO4
    KAMESWARI, S
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1989, 40 (04): : 213 - 218
  • [6] Hot corrosion behavior of CoWSi/WSi2 coating exposed to Na2SO4+NaCl salt at 900 °C
    Mehrizi, M. Zarezadeh
    Eisaabadi, Gh.
    Beygi, R.
    CERAMICS INTERNATIONAL, 2016, 42 (03) : 3959 - 3964
  • [7] Hot corrosion behavior of AlCuFeCr quasicrystalline coating on titanium alloy with the mixture of NaCl and Na2SO4 deposit
    Wang, Fengfeng
    Zhou, Chungen
    Gong, Shengkai
    Xu, Huibin
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2313 - +
  • [8] Hot Corrosion of Fe-Cr Alloys with 75 Na2SO4+25 NaCl Coating at 1173 K
    Fu, Guangyan
    Tang, Xiaopeng
    Liu, Qun
    Su, Yong
    Wang, Xiao
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2012, 31 (06) : 717 - 721
  • [9] Corrosion behavior of the NiCrAlY and NiSiAlY alloys with salt mixtures of NaCl/Na2SO4
    Zheng, Haiyang
    Cui, Tiancheng
    Zhu, Bing
    Yu, Xiaopeng
    Yu, Miao
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2024, 42 (02):
  • [10] Hot Corrosion Behavior of Hf-Doped NiAl Coating in the Mixed Salt of Na2SO4 + K2SO4 at 900 °C
    Zhang, W. L.
    Li, W.
    Fu, L. B.
    Peng, X.
    Sun, J.
    Jiang, S. M.
    Gong, J.
    Sun, C.
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (09) : 1409 - 1420
12345