Metallurgical analysis on a cracked super duplex stainless steel flange

被引：6
|
作者：
Liu T. [1 ]
Zhiyong R.W. [1 ]
Xu D. [1 ]
Aung A.A. [1 ]
机构：
[1] Det Norske Veritas Pte Ltd - Testing Inspection and Certification, Singapore 118227
来源：
Journal of Failure Analysis and Prevention | 2014年 / 14卷 / 04期
关键词：
Brittle cracking; Heat treatment; SEM/EDX; Sigma phase; Super duplex stainless steel;
D O I：
10.1007/s11668-014-9832-4
中图分类号：
学科分类号：
摘要：
A flange-to-pipe weldment in a seawaterintake-return-line suffered from cracking on its flange portion after in service for 4 months. The flange was fabricated from S32750 super duplex stainless steel. The cracked flange was investigated by visual inspection and fractographic examination on the crack surface, metallographic examination, hardness measurement, and chemical composition analysis of the flange-to-pipe weldment. The results of laboratory analysis showed that the flange had cracked in a brittle manner resulting from the presence of large amount of sigma phase in the flange material. Formation of such brittle second phase precipitates in the flange material was due to improper heat treatment. © ASM International 2014.
引用
收藏
页码：470 / 477
页数：7
相关论文
共 50 条
  • [41] Welding of Large Thickness Super Duplex Stainless Steel: Microstructure and Properties
    Bermejo, Maria Asuncion Valiente
    Eyzop, Daniel
    Hurtig, Kjell
    Karlsson, Leif
    [J]. METALS, 2021, 11 (08)
  • [42] Prediction of sigma phase precipitation in super duplex stainless steel weldments
    Nishimoto K.
    Saida K.
    Katsuyama O.
    [J]. Welding in the World, 2006, 50 (3-4) : 13 - 28
  • [43] Nd:YAG Laser Butt Welding of Super Duplex Stainless Steel
    Sivagurumanikandan, N.
    Raghukandan, K.
    Saravanan, S.
    [J]. LASERS IN ENGINEERING, 2016, 35 (1-4) : 217 - 225
  • [44] Hydrogen Embrittlement Enhanced by Plastic Deformation of Super Duplex Stainless Steel
    Elhoud, A.
    Renton, N.
    Deans, W.
    [J]. DAMAGE AND FRACTURE MECHANICS: FAILURE ANALYSIS OF ENGINEERING MATERIALS AND STRUCTURES, 2009, : 59 - +
  • [45] The effect of manufacturing variables on the corrosion resistance of a super duplex stainless steel
    Elhoud, A. M.
    Renton, N. C.
    Deans, W. F.
    [J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2011, 52 (5-8): : 451 - 461
  • [46] Erratum to: Studies on the pore formation in super duplex stainless steel welds
    Juliane Stützer
    Manuela Zinke
    Sven Jüttner
    [J]. Welding in the World, 2017, 61 : 635 - 635
  • [47] On the High Temperature Deformation Behaviour of 2507 Super Duplex Stainless Steel
    Mishra, M. K.
    Balasundar, I.
    Rao, A. G.
    Kashyap, B. P.
    Prabhu, N.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (02) : 802 - 812
  • [48] On the Precipitation of Sigma and Chi Phases in a Cast Super Duplex Stainless Steel
    R. O. Sousa
    P. Lacerda
    P. J. Ferreira
    L. M. M. Ribeiro
    [J]. Metallurgical and Materials Transactions A, 2019, 50 : 4758 - 4778
  • [49] Experiences with Zeron 100 super duplex stainless steel in industrial applications
    Warburton, GR
    Francis, R
    Mockler, C
    [J]. CORROSION REVIEWS, 1998, 16 (03): : 219 - 234
  • [50] Influence of FCAW process parameters in super duplex stainless steel claddings
    Kumar, G. Sathish
    Saravanan, S.
    Balan, A. V.
    Oscar, J.
    Ragunath, R.
    Ramesh, M.
    [J]. MATERIALS TODAY-PROCEEDINGS, 2020, 21 : 63 - 65
12345