Analysis of the Weld Structure for Steel 08Kh18N10T

被引：0
|
作者：
A. M. Apasov
É. V. Kozlov
A. A. Apasov
机构：
[1] Yurga Branch of Tomsk Polytechnical University,
[2] ,undefined
[3] Tomsk State Architecture and Building University,undefined
[4] ,undefined
[5] Yurga Machine Building Plant,undefined
[6] ,undefined
来源：
Metal Science and Heat Treatment | 2001年 / 43卷
关键词：
Steel 08Kh18N10T; Weld Structure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：489 / 492
页数：3
相关论文
共 50 条
  • [41] Formation of a submicrocrystalline structure in austenitic 08Kh18N10T steel during equal-channel angular pressing followed by heating
    Dobatkin S.V.
    Rybal'chenko O.V.
    Raab G.I.
    Russian Metallurgy (Metally), 2006, 2006 (1) : 42 - 48
  • [42] Development of the Acoustic Method for Assessing the Degree of Degradation of 08Kh18N10T Steel at Early Stages of Fatigue Fracture*
    Mishakin, V. V.
    Mitenkov, F. M.
    Klyushnikov, V. A.
    STRENGTH OF MATERIALS, 2014, 46 (05) : 666 - 671
  • [43] COOLING RATE OF 08KH18N10T ROLLED STEEL FLATS DURING HIGH-TEMPERATURE THERMOMECHANICAL TREATMENT
    ZHADAN, VT
    TRUSOV, VA
    SMIRNOV, VM
    PETROVA, EA
    STEEL IN THE USSR, 1980, 10 (09): : 491 - 493
  • [44] Adding Tungsten Semicarbide to 08Kh18N10T Corrosion-Resistant Steel and Its Effect on the Mechanical Properties
    Chumanov I.V.
    Anikeev A.N.
    Sedukhin V.V.
    Steel in Translation, 2022, 52 (02) : 129 - 133
  • [45] THE PROJECTION WELDING OF V3K STELLITE TO 08KH18N10T STEEL IN THE PRODUCTION OF VALVE FITTINGS
    PODOLA, NV
    SKOPENKO, AI
    KRIVOKON, NA
    BOBRIK, VG
    TIMOFEEV, VA
    GOLUBITSKII, VI
    AUTOMATIC WELDING USSR, 1985, 38 (01): : 33 - 35
  • [46] STRAINS IN, AND THE NATURE OF FAILURE OF, BRAZED JOINTS IN THE 08KH18N10T STEEL IN STRUCTURES OF THERMAL POWER-PLANT
    ORLOV, AV
    WELDING PRODUCTION, 1981, 28 (04): : 35 - 37
  • [47] Development of the Acoustic Method for Assessing the Degree of Degradation of 08Kh18N10T Steel at Early Stages of Fatigue Fracture*
    V. V. Mishakin
    F. M. Mitenkov
    V. A. Klyushnikov
    Strength of Materials, 2014, 46 : 666 - 671
  • [48] LOW-CYCLE FATIGUE OF 22K AND 08KH18N10T STEELS AND THEIR WELD JOINTS IN A WATER HEAT CARRIER
    VASILEV, VG
    MANAENKOV, YG
    NIKIFOROV, AD
    TEN, A
    TETERIN, DM
    FILATOV, VM
    SOVIET MATERIALS SCIENCE, 1987, 23 (03): : 322 - 325
  • [49] Gradient structural phase states formed in steel 08Kh18N10T in the course of high-cycle fatigue to failure
    Yu. F. Ivanov
    V. E. Gromov
    S. V. Gorbunov
    S. V. Vorob’ev
    S. V. Konovalov
    The Physics of Metals and Metallography, 2011, 112 : 81 - 89
  • [50] Gradient Structural Phase States Formed in Steel 08Kh18N10T in the Course of High-Cycle Fatigue to Failure
    Ivanov, Yu. F.
    Gromov, V. E.
    Gorbunov, S. V.
    Vorob'ev, S. V.
    Konovalov, S. V.
    PHYSICS OF METALS AND METALLOGRAPHY, 2011, 112 (01): : 81 - 89
12345