Preparation of nanosized crystalline TiO2 particles at low temperature for photocatalysis

被引：0
|
作者：
S. Watson
D. Beydoun
J. Scott
R. Amal
机构：
[1] The University of New South Wales,Centre for Particle and Catalyst Technologies, School of Chemical Engineering and Industrial Chemistry
来源：
Journal of Nanoparticle Research | 2004年 / 6卷
关键词：
nanoparticles; photocatalysis; TiO; rutile; anatase; brookite; particle preparation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Nanocrystalline titanium dioxide (TiO2) particles were prepared by a modified alkoxide method under acidic conditions at temperatures ranging from 60°C to 90°C. The reaction temperature was used to control the crystalline phase of the TiO2 particles. At 60°C and 75°C rutile was formed whilst at 90°C anatase and brookite were formed.
引用
收藏
页码：193 / 207
页数：14
相关论文
共 50 条
  • [41] Preparation and photocatalysis of TiO2 nanoparticles doped with nitrogen and cadmium
    Wu Pingxiao
    Tang Jianwen
    Dang Zhi
    MATERIALS CHEMISTRY AND PHYSICS, 2007, 103 (2-3) : 264 - 269
  • [42] Preparation and Photocatalysis Properties of Bipyramid Nanocrystal TiO2 Microtubules
    Zhao Jing-Xian
    Li Qiao-Ling
    Zhang Gun-Rui
    Li Bao-Dong
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2009, 25 (05) : 875 - 879
  • [43] The preparation and characterization of TiO2 ultrafine particles
    Xu, ZL
    Shang, J
    Liu, CM
    Kang, CL
    Guo, HC
    Du, YG
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1999, 63 (03): : 211 - 214
  • [44] Preparation of the AC/TiO2 Composite Particles in Normal Temperature and Degradation of TNT
    Cui Haiping
    Yan Jun
    Du Shiguo
    Wang Mingqiu
    CHEMICAL ENGINEERING AND MATERIAL PROPERTIES, PTS 1 AND 2, 2012, 391-392 : 964 - +
  • [45] TIO2 ULTRAFINE PARTICLES - PREPARATION AND CHARACTERIZATION
    KAMINISHI, S
    KOMOGUCHI, S
    MORITA, T
    NAKAJIMA, Y
    SHARP TECHNICAL JOURNAL, 1987, (38): : 13 - 17
  • [46] Preparation of Sandwich-like TiO2/Graphene/TiO2 films and Its Application in Photocatalysis
    Wu, Hongpeng
    He, Dawei
    Wang, Yongsheng
    Yang, Bingyang
    Xu, Haiteng
    Li, Jingfeng
    Wang, Haiteng
    Wang, Jigang
    Fu, Ming
    ADVANCED IN NANOSCIENCE AND TECHNOLOGY, 2012, 465 : 80 - 85
  • [47] Low-temperature synthesis of nanometer-sized crystalline TiO2 particles and their photoinduced decomposition of formic acid
    Ito, S
    Inoue, S
    Kawada, H
    Hara, M
    Iwasaki, M
    Tada, H
    JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1999, 216 (01) : 59 - 64
  • [48] Preparation and characterization of ZnO/TiO2, SO42-/ZnO/TiO2 photocatalyst and their photocatalysis
    Liao, SJ
    Huang, DG
    Yu, DH
    Su, YL
    Yuan, GQ
    JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 2004, 168 (1-2) : 7 - 13
  • [49] Room-temperature preparation of crystalline TiO2 thin films and their applications in polymer/TiO2 hybrid optoelectronic devices
    Wu, Chung-Han
    Li, Hanying
    Fong, Hon Hang
    Pozdin, Vladimir A.
    Estroff, Lara A.
    Malliaras, George G.
    ORGANIC ELECTRONICS, 2011, 12 (06) : 1073 - 1079
  • [50] The adhesion and shape of nanosized Au particles in a Au/TiO2 catalyst
    Lopez, N
    Norskov, JK
    Janssens, TVW
    Carlsson, A
    Puig-Molina, A
    Clausen, BS
    Grunwaldt, JD
    JOURNAL OF CATALYSIS, 2004, 225 (01) : 86 - 94
12345