Role of Tungsten in the Tempered Martensite Embrittlement of a Modified 9 Pct Cr Steel

被引:0
|
作者
Alexandra Fedoseeva
Nadezhda Dudova
Rustam Kaibyshev
机构
[1] Belgorod State University,
来源
Metallurgical and Materials Transactions A | 2017年 / 48卷
关键词
Intergranular Fracture; Intergranular Crack; M23C6 Carbide; Martensitic Matrix; Initiation Zone;
D O I
暂无
中图分类号
学科分类号
摘要
The effect of tempering on the mechanical properties and fracture behavior of two 3 pct Co-modified 9 pct Cr steels with 2 and 3 wt pct W was examined. Both steels were ductile in tension tests and tough under impact tests in high-temperature tempered conditions. At T ≤ 923 K (650 °C), the addition of 1 wt pct W led to low toughness and pronounced embrittlement. The 9Cr2W steel was tough after low-temperature tempering up to 723 K (450 °C). At 798 K (525 °C), the decomposition of retained austenite induced the formation of discontinuous and continuous films of M23C6 carbides along boundaries in the 9Cr2W and the 9Cr3W steels, respectively, which led to tempered martensite embrittlement (TME). In the 9Cr2W steel, the discontinuous boundary films played a role of crack initiation sites, and the absorption energy was 24 J cm−2. In the 9Cr3W steel, continuous films provided a fracture path along the boundaries of prior austenite grains (PAG) and interlath boundaries in addition that caused the drop of impact energy to 6 J cm−2. Tempering at 1023 K (750 °C) completely eliminated TME by spheroidization and the growth of M23C6 carbides, and both steels exhibited high values of adsorbed energy of ≥230 J cm−2. The addition of 1 wt pct W extended the temperature domain of TME up to 923 K (650 °C) through the formation of W segregations at boundaries that hindered the spheroidization of M23C6 carbides.
引用
收藏
页码:982 / 998
页数:16
相关论文
共 50 条
  • [21] Characterization of Ferrite in Tempered Martensite of Modified 9Cr-1Mo Steel Using the Electron Backscattered Diffraction Technique
    C. R. Das
    S. K. Albert
    A. K. Bhaduri
    B. S. Murty
    Metallurgical and Materials Transactions A, 2011, 42 : 3849 - 3852
  • [22] Characterization of Ferrite in Tempered Martensite of Modified 9Cr-1Mo Steel Using the Electron Backscattered Diffraction Technique
    Das, C. R.
    Albert, S. K.
    Bhaduri, A. K.
    Murty, B. S.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (13): : 3849 - 3852
  • [23] INFLUENCE OF TEMPERED MARTENSITE EMBRITTLEMENT ON MECHANICAL PROPERTIES OF HIGH STRENGTH 4340 STEEL
    KULA, EB
    MATERIALS RESEARCH AND STANDARDS, 1968, 8 (08): : 36 - &
  • [24] TEMPERED MARTENSITE EMBRITTLEMENT AND INTERGRANULAR FRACTURE IN AN ULTRAHIGH STRENGTH SULFUR DOPED STEEL
    BRIANT, CL
    BANERJI, SK
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (02): : 309 - 319
  • [25] EVALUATION OF TEMPERED MARTENSITE EMBRITTLEMENT IN AISI 15B41 STEEL
    LESCANO, D
    MANCINI, R
    LANZILLOTTO, C
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1995, 14 (17) : 1241 - 1242
  • [26] Effects of precipitation on the scale and grain growth in 9% Cr tempered martensite steel upon steam oxidation
    Ma, Houyu
    He, Yinsheng
    Liu, Yue
    Shin, Keesam
    MATERIALS CHARACTERIZATION, 2020, 167
  • [27] Effect of Mn Content on Hydrogen Embrittlement Resistance of Tempered Martensite in Low Alloy Steel
    Yoshida S.
    Arai Y.
    Omura T.
    Cho K.
    Yasuda H.Y.
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 2024, 110 (04): : 385 - 394
  • [28] Study of microestructure and tempered martensite embrittlement in AISI 15B41 steel
    Lescano, D. E.
    Silvetti, S. P.
    11TH INTERNATIONAL CONGRESS ON METALLURGY & MATERIALS SAM/CONAMET 2011, 2012, 1 : 134 - 140
  • [29] Creep Degradation Processes in Tungsten Modified 9%Cr Martensitic Steel
    Sklenicka, V.
    Kral, P.
    Kucharova, K.
    Kvapilova, M.
    Dvorak, J.
    PROCEEDINGS OF THE FIRST INTERNATIONAL CONFERENCE ON THEORETICAL, APPLIED AND EXPERIMENTAL MECHANICS, 2019, 5 : 93 - 94
  • [30] ROLE OF CARBON IN EMBRITTLEMENT PHENOMENA OF TEMPERED MARTENSITIC 12CR-0.15-PERCENT-C STEEL
    PRABHUGAUNKAR, GV
    HUNTZ, AM
    LACOMBE, P
    METAL SCIENCE, 1980, 14 (07): : 241 - 252