Wear and corrosion resistance of electroless plating Ni-P coating on P110 steel

被引：0
|
作者：
Naiming Lin
Peng Zhou
Jiaojuan Zou
Faqin Xie
Bin Tang
机构：
[1] Taiyuan University of Technology,Research Institute of Surface Engineering
[2] Northwestern Polytechnical University,School of Aeronautics
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2015年 / 30卷
关键词：
wear; corrosion; electroless plating; Ni-P coating; P110 steel;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In order to improve the surface performance and increase the lifetime of P110 oil casing tube steel during operation, electroless plating was conducted to form Ni-P coating onto its surface. The surface morphology/element distribution and phase constitution of the Ni-P coating were analyzed using scanning electron microscope (SEM) equipped with energy dispersive spectrometry (EDS) and X-ray diffraction (XRD). Tribological and electrochemical measurement tests were applied to investigate the wear and corrosion resistance of P110 steel and the Ni-P coating. The results showed that a uniform and compact, high phosphorous Ni-P coating was formed. The obtained Ni-P coating indicated certain friction-reduction effect and lower mass loss during friction-wear tests. The Ni-P coating also exhibited higher corrosion resistance in comparison with bared P110 steel. The obtained Ni-P coating has significantly improved the surface performance of P110 steel.
引用
收藏
页码：622 / 625
页数：3
相关论文
共 50 条
  • [21] The effect of hydrogen on friction and wear of Ni-P electroless coating
    Zhou, Qing-Jun
    Zhao, Jian-Qiang
    Nie, Fei
    Chu, Wu-Yang
    Li, Jin-Xu
    Qiao, Li-Jie
    WEAR, 2009, 266 (7-8) : 810 - 813
  • [22] STUDY OF THE FRICTION AND WEAR BEHAVIOR OF ELECTROLESS NI-P COATING
    YU, LG
    ZHANG, XS
    THIN SOLID FILMS, 1993, 229 (01) : 76 - 82
  • [23] Comparison on tribological properties between Cu coating and Ni-P coating on P110 oil tube steel substrate
    Yao, X.-F. (yxf933@126.com), 1600, Science Press (32):
  • [24] Deposition mechanism of wastewater-free electroless nickel plating on magnesium alloy and corrosion resistance of Ni-P coating
    Fang, X.-X. (fangxinxian@njit.edu.cn), 1819, Central South University of Technology (23):
  • [25] Variation of solution composition during electroless plating of Ni-P coating
    Huazhong Ligong Daxue Xuebao/Journal Huazhong (Central China) University of Science and Technology, 1995, 23 (01):
  • [26] Corrosion Characteristics of Electroless Ni-P Coating in Naphthenic Acid
    Chen, Zhiliang
    Lin, An
    Gan, Fuxing
    Fang, Dajing
    Hao, Long
    Zhang, Yeming
    MATERIALS PERFORMANCE, 2009, 48 (04) : 38 - 42
  • [27] Optimization of process parameters to improve the wear resistance of the mild steel using electroless Ni-P coating process
    Kumar, Vinod T.
    Muraliraja, R.
    Chandrasekaran, M.
    JURNAL TRIBOLOGI, 2021, 31 : 1 - 12
  • [28] Corrosion characteristics of electroless Ni-P coating in naphthenic acid
    Department of Environmental Engineering, Wuhan, China
    不详
    不详
    Mater Perform, 2009, 4 (38-42):
  • [29] Wear and Corrosion Investigation on the Electrodeposited Ni-P Coating
    Lee, H. B.
    Lin, C. S.
    Wuu, D. S.
    Lee, C. Y.
    TRIBOLOGY TRANSACTIONS, 2011, 54 (04) : 497 - 504
  • [30] Elimination of the corrosion of Ni-P substrates during electroless gold plating
    Shaigan, N
    Ashrafizadeh, SN
    Bafghi, MSH
    Rastegari, S
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2005, 152 (04) : C173 - C178
12345