Micromechanics of Damage Accumulation in a 2.5D Woven C-Fiber/SiC Ceramic Composite

被引：0
|
作者：
N. Jekabsons
J. Varna
机构：
[1] University of Technology,Div. of Polymer Engineering, Luleå
来源：
Mechanics of Composite Materials | 2001年 / 37卷
关键词：
ceramic composite; SiC; damage; microdamage; tensile test; micromechanics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The morphology of a C/PyC/SiC ceramic composite is studied and its microdamage mechanisms are revealed. Some models based on the micromechanical fracture mechanics are proposed to describe the possible damage processes. The influence of the observed microdamage on the stiffness reduction is studied. It is shown that the delamination between the layers and the cracks in the coating alone cannot explain the stiffness reduction observed in tests. Debonding between the SiC coating and pyrocarbon is suggested as another mechanism of the stiffness reduction.
引用
收藏
页码：289 / 298
页数：9
相关论文
共 50 条
  • [31] Impact behaviors and damage mechanisms of 2.5D woven composites: Experiment and simulation
    Dong, Fang
    Yuan, Qiong
    Liu, Jingyan
    Qian, Kun
    Sun, Jin
    Zhang, Diantang
    JOURNAL OF INDUSTRIAL TEXTILES, 2022, 52
  • [32] Damage theoretical analysis of 2.5D C/SiC Composites under Tensile and Shear Loading
    Chang, Yanjun
    Zhang, Keshi
    Jiao, Guiqiong
    Chen, Jianyun
    ADVANCES IN COMPOSITES, PTS 1 AND 2, 2011, 150-151 : 330 - +
  • [33] FEM Simulation of Single-Grit Grinding on a 2.5D Woven Composite
    Yuguo Wang
    Chao Ding
    Bin Lin
    Transactions of Tianjin University, 2017, 23 (06) : 538 - 546
  • [34] FEM Simulation of Single-Grit Grinding on a 2.5D Woven Composite
    Yuguo Wang
    Chao Ding
    Bin Lin
    Transactions of Tianjin University, 2017, (06) : 538 - 546
  • [35] FEM Simulation of Single-Grit Grinding on a 2.5D Woven Composite
    Wang Y.
    Ding C.
    Lin B.
    Transactions of Tianjin University, 2017, 23 (6) : 538 - 546
  • [36] Multiscale Simulation on Tensile Failure Analysis of 2.5D C/SiC Composite Orifice Plate
    Du X.-Y.
    Gao X.-G.
    Song Y.-D.
    Tuijin Jishu/Journal of Propulsion Technology, 2020, 41 (02): : 439 - 446
  • [37] Analytical model of elastic modulus and coefficient of thermal expansion for 2.5D C/SiC composite
    Chunyuan Kong
    Zhigang Sun
    Xuming Niu
    Yingdong Song
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2013, 28 : 494 - 499
  • [38] Analytical model of elastic modulus and coefficient of thermal expansion for 2.5D C/SiC composite
    Kong Chunyuan
    Sun Zhigang
    Niu Xuming
    Song Yingdong
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2013, 28 (03): : 494 - 499
  • [39] Analytical Model of Elastic Modulus and Coefficient of Thermal Expansion for 2.5D C/SiC Composite
    孔春元
    孙志刚
    NIU Xuming
    SONG Yingdong
    Journal of Wuhan University of Technology(Materials Science Edition), 2013, 28 (03) : 494 - 499
  • [40] Comparison of ballistic impact behaviors between plain woven and 2.5D woven fabric composite plates
    Feng Z.
    Chi Q.
    Cui H.
    Xie J.
    Mu H.
    Hangkong Xuebao/Acta Aeronautica et Astronautica Sinica, 2022, 43 (05):
12345