Research in the Area of Preparing Materials Based on Fuzed Quartz HCBS. Part 3. Study and Improvement of Centrifugal Casting1

被引：0

作者：

Yu. E. Pivinskii

机构：

[1] OOO NVF Kerambet-Ogneupor,

来源：

Refractories and Industrial Ceramics | 2015年 / 56卷

关键词：

centrifugal casting; fuzed quartz HCBS; ceramic concretes; volume concentration; excess factor; quartz steel-pouring refractories; casting regime; peripheral velocity;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Chronology is considered for development of research and introductory work in the field of centrifugal casting, implemented in the production of quartz steel-pouring refractories. Large scale application of centrifugal casting is used for the first time in domestic and overseas practice for ceramic and refractory production. The main requirements are considered for original casting systems and regimes making it possible to obtain high density semifinished product. Prospects are shown in a number of examples of using the method in casting objects based on HCBS of other materials.

引用

页码：126 / 135

页数：9

共 50 条

[21] Research in the Area of Preparing Materials Based on Fuzed Quartz HCBS. Part 9. Effect of Alkali Additions on Material Cristobalitization and Thermal Expansion After Nonisothermal Heating1
Yu. E. Pivinskii
P. V. Dyakin
A. Yu. Kolobov
Refractories and Industrial Ceramics, 2016, 57 : 135 - 140
[22] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 11. Composite Composition HCBS (Fuzed Corundum-Bauxite, Sintered Bauxite, Quartz Glass) and Some Properties of Materials Based Upon Them1
Yu. E. Pivinskii
P. V. Dyakin
L. V. Ostryakov
Refractories and Industrial Ceramics, 2017, 58 : 450 - 456
[23] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 9. Preparation and Properties of Mixed HCBS Composition: Fuzed Bauxite-Corundum, Quartz Glass, Reactive Alumina. Dilatometric Study of Materials Based on Them
Yu. E. Pivinskii
P. V. Dyakin
A. Yu. Kolobov
Refractories and Industrial Ceramics, 2017, 58 : 103 - 108
[24] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 11. Composite Composition HCBS (Fuzed Corundum-Bauxite, Sintered Bauxite, Quartz Glass) and Some Properties of Materials Based Upon Them1
Pivinskii, Yu. E.
Dyakin, P. V.
Ostryakov, L. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2017, 58 (04) : 450 - 456
[25] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 9. Preparation and Properties of Mixed HCBS Composition: Fuzed Bauxite-Corundum, Quartz Glass, Reactive Alumina. Dilatometric Study of Materials Based on Them
Pivinskii, Yu. E.
Dyakin, P. V.
Kolobov, A. Yu.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2017, 58 (01) : 103 - 108
[26] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 10. Effect of Firing Temperature on Properties of Materials Prepared Based on Mixed Composition HCBS from Fuzed Bauxite-Corundum, Quartz Glass, and Reactive Alumina1
Yu. E. Pivinskii
P. V. Dyakin
A. M. Gorokhovskii
L. V. Ostryakov
Refractories and Industrial Ceramics, 2017, 58 : 227 - 232
[27] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 3. Effect of Firing Temperature on Sintering and Mullitization of Materials Prepared on the Basis of Composite Composition HCBS1
Pivinskii, Yu. E.
Dyakin, P. V.
Ostryakov, L. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2016, 56 (06) : 648 - 655
[28] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 10. Effect of Firing Temperature on Properties of Materials Prepared Based on Mixed Composition HCBS from Fuzed Bauxite-Corundum, Quartz Glass, and Reactive Alumina1
Pivinskii, Yu. E.
Dyakin, P. V.
Gorokhovskii, A. M.
Ostryakov, L. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2017, 58 (02) : 227 - 232
[29] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 3. Effect of Firing Temperature on Sintering and Mullitization of Materials Prepared on the Basis of Composite Composition HCBS1
Yu. E. Pivinskii
P. V. Dyakin
L. V. Ostryakov
Refractories and Industrial Ceramics, 2016, 56 : 648 - 655
[30] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 6. Mullitization and Thermal Expansion of Materials Based on Compound Composition HCBS1
Pivinskii, Yu. E.
Dyakin, P. V.
Kolobov, A. Yu.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2016, 57 (03) : 297 - 303

← 1 2 3 4 5 →