Corrosion and Corrosion-Mechanical Fracture of the Steel of Crude-Oil Tanks

被引：0
|
作者：
D. Yu. Petryna
V. M. Hohol’
Yu. D. Petryna
O. I. Zvirko
Yu. M. Nykyforchyn
机构：
[1] Ivano-Frankivs’k National Technical University of Oil and Gas,Karpenko Physicomechanical Institute
[2] Ukrainian National Academy of Sciences,undefined
来源：
Materials Science | 2016年 / 51卷
关键词：
long-term operation; corrosion; tank; degradation; crude oil; bottom water;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We establish the influence of long-term operation of an RVS-1000 tank for crude oil on the corrosion resistance, resistance to corrosion-mechanical fracture, and susceptibility to brittle fracture of St3sp steel from different parts of the wall and bottom of the structure. The worst characteristics are exhibited by the metal operating in continuous contact with bottom or condensed water. We analyze the corrosive action of bottom waters of the Nadvirna and Rozhnyativ oil used at the “Naftokhimik Prykarpattya” Joint-Stock Company on the corrosion and crack resistances of steel.
引用
收藏
页码：666 / 672
页数：6
相关论文
共 50 条
  • [41] Structural sensitivity of steels to corrosion-mechanical fracture under conditions of fatigue and cavitation
    O. T. Tsyrul'nyk
    A. I. Bassarab
    [J]. Materials Science, 1999, 35 : 581 - 586
  • [42] Effect of inhibitors on the corrosion-mechanical fracture of steels in hydrogen-sulfide media
    Radkevych, OI
    Dominyuk, IM
    Tsynman, AI
    [J]. MATERIALS SCIENCE, 2002, 38 (01) : 126 - 131
  • [43] Crude oil corrosion
    Bailey, G.
    Palmer, J.W.
    [J]. Hydrocarbon Engineering, 2002, 7 (03):
  • [44] Effect of Inhibitors on the Corrosion-Mechanical Fracture of Steels in Hydrogen-Sulfide Media
    O. I. Radkevych
    I. M. Dominyuk
    A. I. Tsynman
    [J]. Materials Science, 2002, 38 : 126 - 131
  • [45] Structural sensitivity of steels to corrosion-mechanical fracture under conditions of fatigue and cavitation
    Tsyrul'nyk, OT
    Bassarab, AI
    [J]. MATERIALS SCIENCE, 1999, 35 (04) : 581 - 586
  • [46] Corrosion-mechanical resistance of pipe steel in hydrogen-sulfide containing media
    O. I. Radkevych
    O. S. P’yasets’kyi
    I. I. Vasylenko
    [J]. Materials Science, 2000, 36 : 425 - 430
  • [47] Corrosion-mechanical properties of materials for reactor vessels
    Pokhmurs'kyi, VI
    Bilyi, LM
    Khoma, MS
    [J]. MATERIALS SCIENCE, 2001, 37 (03) : 499 - 508
  • [48] On concentration galvanic elements in corrosion-mechanical cracks
    L. N. Petrov
    V. G. Zakharchuk
    K. Sulek
    B. Szczegelnjak
    [J]. Materials Science, 1999, 35 : 232 - 236
  • [49] Corrosion-Mechanical Properties of Materials for Reactor Vessels
    V. I. Pokhmurs'kyi
    L. M. Bilyi
    M. S. Khoma
    [J]. Materials Science, 2001, 37 : 499 - 508
  • [50] Special Issue on Corrosion-Mechanical Loading Interactions
    Wouters, Y.
    Pint, B.
    Monceau, D.
    [J]. OXIDATION OF METALS, 2017, 88 (01): : 1 - 2
12345