Surface organic modification of Fe3O4 magnetic nanoparticles

被引：0
|
作者：
Sheng Cui
Xiaodong Shen
Benlan Lin
Guodong Jiang
Weihua Zhang
机构：
[1] Nanjing University of Technology,College of Material Science and Technology
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2008年 / 23卷
关键词：
Fe; O; nanoparticles; KH570; surface organic modification; chemical adsorb; dispersivity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The surface organic modification of Fe3O4 nanoparticles with silane coupling reagent KH570 was studied. The modified and unmodified nanoparticles were characterized by FT-IR, XPS and TEM. The spectra of FT-IR and XPS revealed that KH570 was coated onto the surface of Fe3O4 nanoparticles to get Fe-OSi bond and an organic coating layer also was formed. Fe3O4 nanoparticles were spheres partly with mean size of 18.8 nm studied by TEM, which was consistent with the result 17.9 nm calculated by Scherrer’s equation. KH570 was adsorbed on surface and formed chemistry bond to be steric hindrance repulsion which prevented nanoparticles from reuniting. Then glycol-based Fe3O4 magnetic liquids dispersed stably was gained.
引用
收藏
页码：436 / 439
页数：3
相关论文
共 50 条
  • [21] Modification of Fe3O4 nanoparticles with carboranes
    Tulebayeva, D. Zh
    Kozlovskiy, A. L.
    Korolkov, I. V.
    Gorin, Y. G.
    Kazantsev, A. V.
    Abylgazina, L.
    Shumskaya, E. E.
    Kaniukov, E. Y.
    Zdorovets, M. V.
    MATERIALS RESEARCH EXPRESS, 2018, 5 (10):
  • [22] Covalent surface modification of Fe3O4 magnetic nanoparticles with alkoxy silanes and amino acids
    Demin, Alexander M.
    Krasnov, Victor P.
    Charushin, Valery N.
    MENDELEEV COMMUNICATIONS, 2013, 23 (01) : 14 - 16
  • [23] SURFACE MODIFICATION AND CHARACTERIZATION OF Fe3O4/Au COMPOSITE NANOPARTICLES
    Shi, Feng
    Hui, Wenli
    Cui, Yali
    Chen, Chao
    NANO, 2011, 6 (02) : 145 - 151
  • [24] Surface modification and characterization of Fe3O4/Au composite nanoparticles
    Shi, Feng
    Hui, Wenli
    Chen, Chao
    Cui, Yali
    JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2011, 13 (1-2): : 141 - 145
  • [25] Synthesis of magnetic nanoparticles of Fe3O4 and CoFe2O4 and their surface modification by surfactant adsorption
    Zhao, SY
    Lee, DK
    Kim, CW
    Cha, RG
    Kim, YH
    Kang, YS
    BULLETIN OF THE KOREAN CHEMICAL SOCIETY, 2006, 27 (02) : 237 - 242
  • [26] Synthesis of magnetic nanoparticles of Fe3O4 and CoFe2O4 and their surface modification by surfactant adsorption
    Department of Chemistry, Pukyong National University, Busan 608-737, Korea, Republic of
    不详
    Bull. Korean Chem. Soc., 2006, 2 (237-242):
  • [27] Surface modification of Fe3O4 nanoparticles prepared in high temperture organic solution by sodium oleate
    Ding Jian-Fang
    Jiang Ji-Sen
    JOURNAL OF INORGANIC MATERIALS, 2007, 22 (05) : 859 - 863
  • [28] Effect of Surface Modification on Cellular Internalization of Fe3O4 Nanoparticles in Strong Static Magnetic Field
    Lei, Wang
    Min, Wang
    Hui, Dal
    Yun, Liu
    An, Xu
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2015, 15 (07) : 5184 - 5192
  • [29] High field surface magnetic study of Fe3O4 nanoparticles
    Kihal, A.
    Fillion, G.
    Bouzabata, B.
    Barbara, B.
    PHYSICA STATUS SOLIDI B-BASIC SOLID STATE PHYSICS, 2012, 249 (03): : 604 - 614
  • [30] Preparation, surface functionalization and application of Fe3O4 magnetic nanoparticles
    Liu, Shixiang
    Yu, Bing
    Wang, Song
    Shen, Youqing
    Cong, Hailin
    ADVANCES IN COLLOID AND INTERFACE SCIENCE, 2020, 281
12345