Effect of temperature on the fracture mechanisms of 8090 Al-Li alloy and 8090 Al-Li/SiC composite

被引：13
|
作者：
González, C [1 ]
Martín, A [1 ]
Llorca, J [1 ]
机构：
[1] Univ Politecn Madrid, ETS Ingn Caminos, Dept Mat Sci, E-28040 Madrid, Spain
来源：
SCRIPTA MATERIALIA | 2004年 / 51卷 / 11期
关键词：
Al-Li alloys; metal matrix composites; temperature; fracture;
D O I：
10.1016/j.scriptamat.2004.07.025
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The fracture mechanisms in tension were analyzed in a peak-aged 8090 Al-Li alloy and 8090 Al-Li/SiC as a function of temperature. Failure in the alloy changed from intergranular fracture at ambient temperature to ductile void growth above 150 degreesC, leading to a tenfold increase in the elongation to failure. Damage in the composite was always nucleated by particle fracture, and the ductility, which was controlled by the onset of plastic instability, increased moderately with temperature. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：1111 / 1115
页数：5
相关论文
共 50 条
  • [21] Fracture toughness and fatigue crack propagation behavior of 8090 Al-Li alloy
    Burzic, Z
    Sedmak, S
    Maksimovic, S
    Grahovac, N
    Curovic, J
    Stefanovic, V
    MATERIALS SCIENCE, 1995, 31 (01) : 39 - 53
  • [22] FATIGUE BEHAVIOR OF THE AL-LI ALLOY 8090 COMPARED TO 2024
    PETERS, M
    BACHMANN, V
    WELPMANN, K
    ZEITSCHRIFT FUR WERKSTOFFTECHNIK-MATERIALS TECHNOLOGY AND TESTING, 1987, 18 (08): : 277 - 283
  • [23] Investigation on heat treatment technology for 8090 Al-Li alloy
    Shanghai Jiaotong Daxue Xuebao, 1 (76-79):
  • [24] Fracture Toughness and Fatigue Crack Propagation Behavior of Al-Li 8090 Alloy
    Burzic, Z.
    Sedmak, S.
    Maksimovic, S.
    Grahovac, N.
    Materials Science, 1995, 31 (01)
  • [25] STATIC AND DYNAMIC FRACTURE-TOUGHNESS OF AN AL-LI 8090 ALLOY PLATE
    PRASAD, NE
    KAMAT, SV
    MALAKONDAIAH, G
    KUTUMBARAO, VV
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (04) : 441 - 450
  • [26] DEVELOPMENT OF SUPERPLASTICITY IN 8090 AL-LI ALLOY BY STATIC RECRYSTALLIZATION
    SHIN, DH
    SHIN, YH
    CHANG, YW
    MAENG, SC
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (01): : 117 - 121
  • [27] Precipitation of S prime phase in an 8090 Al-Li alloy
    Zheng, Ziqiao
    Hori, S.
    Transactions of Nonferrous Metals Society of China, 1992, 2 (03):
  • [28] LOW-TEMPERATURE SUPERPLASTICITY IN 8090 AL-LI ALLOYS
    PU, HP
    HUANG, JC
    SCRIPTA METALLURGICA ET MATERIALIA, 1993, 28 (09): : 1125 - 1130
  • [29] Microstructural changes during high temperature deformation of an Al-Li(8090) alloy
    Eddahbi, M
    Carreno, F
    Ruano, OA
    SCRIPTA MATERIALIA, 1998, 38 (11) : 1717 - 1723
  • [30] Effects of temperature on the fatigue crack growth of an Al-Li 8090 alloy with δ′ microstructure
    Lee, Chong Soo
    Park, Ki Jong
    Li, Daoming
    Kim, Nack Joon
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1997, 28 A (04): : 1089 - 1093
12345