Enhanced visible photoluminescence of V2O5 via coupling ZnO/V2O5 composite nanostructures

被引：18
|
作者：
Zou, C. W. [1 ]
Yan, X. D. [1 ]
Bian, J. M. [2 ]
Gao, W. [1 ]
机构：
[1] Univ Auckland, Sch Engn, Auckland 1, New Zealand
[2] Dalian Univ Technol, Sch Phys & Optoelect Engn, Dalian 116024, Peoples R China
来源：
OPTICS LETTERS | 2010年 / 35卷 / 08期
关键词：
VANADIUM-OXIDES; THIN-FILMS; ZEOLITE; STATE;
D O I：
10.1364/OL.35.001145
中图分类号：
O43 [光学];
学科分类号：
070207 ; 0803 ;
摘要：
V2O5 films capped by a thin ZnO layer had been prepared by sputtering method at room temperature. The initial smooth films transferred to porous composite nanocrystals and nanorods after annealed at 500 degrees C, and enhanced visible light emission was observed. This tremendous enhancement was attributed to the coupling between V2O5 nanorods and ZnO nanoparticles as well as the improved V2O5 crystallinity. Prominent vibrational fine structures of the photoluminescence spectra were also observed. (C) 2010 Optical Society of America
引用
收藏
页码：1145 / 1147
页数：3
相关论文
共 50 条
  • [31] Photoluminescence and structural analysis of wurtzite (ZnO)(1-x)(V2O5)(x) composite
    Iqbal, Amjid
    Mahmood, Arshad
    Raza, Q.
    Shah, A.
    Rashid, Rashad
    Ali, Zahid
    Malik, A.
    Aziz, U.
    JOURNAL OF SEMICONDUCTORS, 2018, 39 (08)
  • [32] Defect related photoluminescence study of V2O5: Dy3+ nanostructures
    Navyashree, G. R.
    Sunitha, D. V.
    Hareesh, K.
    Nagaraju, G.
    OPTIK, 2020, 206
  • [33] Conversion of V2O5•xH2O into orthorhombic V2O5 single-crystalline nanobelts
    Ding, Jie
    Peng, Hongrui
    Li, Guicun
    Chen, Kezheng
    MATERIALS LETTERS, 2010, 64 (14) : 1562 - 1565
  • [34] Effect of annealing on the microstructure and optical properties of ZnO/V2O5 composite
    Zou, C. W.
    Yan, X. D.
    Chen, R. Q.
    Wu, Z. Y.
    Alyamani, A.
    Gao, W.
    APPLIED PHYSICS LETTERS, 2011, 98 (11)
  • [35] Solution synthesis and electrochemical properties of V2O5 nanostructures
    Takahashi, K
    Wang, Y
    Lee, K
    Cao, GZ
    SOLID STATE IONICS-2004, 2005, 835 : 327 - 332
  • [36] MICROWAVE HALL-MOBILITY MEASUREMENTS ON VANADIUM BRONZE V2O5(NA0.33 V2O5 AND CU0.0083 V2O5)
    SAYED, MM
    PERLSTEIN, JH
    ELECTRONICS LETTERS, 1974, 10 (10) : 178 - 179
  • [37] MECHANOCHEMICAL REDUCTION OF V2O5
    YANG, H
    MCCORMICK, PG
    JOURNAL OF SOLID STATE CHEMISTRY, 1994, 110 (01) : 136 - 141
  • [38] A REFINEMENT OF THE STRUCTURE OF V2O5
    ENJALBERT, R
    GALY, J
    ACTA CRYSTALLOGRAPHICA SECTION C-STRUCTURAL CHEMISTRY, 1986, 42 : 1467 - 1469
  • [39] INTERCALATION OF MG IN V2O5
    YU, WH
    WANG, DZ
    ZHU, B
    ZHOU, GE
    SOLID STATE COMMUNICATIONS, 1987, 63 (11) : 1043 - 1044
  • [40] Effect of the extent of reduction of V2O5 on the adsorption of propylene and the oxidative dehydrogenation of propane to give propylene on V2O5 and V2O5/TiO 2-SiO2
    Red'kina A.V.
    Belokopytov Yu.V.
    Konovalova N.D.
    Khomenko K.N.
    Theoretical and Experimental Chemistry, 2007, 43 (6) : 405 - 410
12345