Fatigue surface crack growth in cylindrical specimen under combined loading

被引：38
|
作者：
Citarella, R. [1 ]
Lepore, M. [1 ]
Shlyannikov, V. [2 ]
Yarullin, R. [2 ]
机构：
[1] Univ Salerno, Dept Ind Engn, Fisciano, SA, Italy
[2] Russian Acad Sci, Res Ctr Power Engn Problems, Kazan 420111, Russia
来源：
ENGINEERING FRACTURE MECHANICS | 2014年 / 131卷
基金：
俄罗斯科学基金会;
关键词：
Surface flaw; Tension and torsion; Crack growth rate; Crack path; DBEM; BOUNDARY-ELEMENT METHOD; FEM; PROPAGATION; TORSION; DBEM; BEM;
D O I：
10.1016/j.engfracmech.2014.08.017
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The subject for studies is a steel bar of circular cross-section with straight-fronted edge notch undergoing fatigue loads. Both the optical microscope measurements and the crack opening displacement (COD) method are used to monitor and investigate both crack depth and crack length during the tests. The variation of crack growth behavior is studied under cyclic axial and combined tension + torsion fatigue loading. Results show that cyclic Mode III loading superimposed on the cyclic Mode I leads to a fatigue life reduction. In parallel to the experimental activity, numerical calculations are performed based on three-dimensional DBEM analysis to determine the stress intensity factors along curvilinear surface crack front and fatigue life prediction. The experimental fatigue crack growth results obtained from round bar specimens have been compared with the numerical predictions. The computational DBEM results are found to be in satisfactory agreement with the experimental findings. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：439 / 453
页数：15
相关论文
共 50 条
  • [31] FATIGUE CRACK-GROWTH UNDER COMPRESSIVE LOADING
    FLECK, NA
    SHIN, CS
    SMITH, RA
    ENGINEERING FRACTURE MECHANICS, 1985, 21 (01) : 173 - +
  • [32] Fatigue crack growth with overload under spectrum loading
    Huang, XP
    Zhang, JB
    Cui, WC
    Leng, JX
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2005, 44 (02) : 105 - 115
  • [33] Fatigue crack growth in ferroelectrics under electrical loading
    Shieh, J
    Huber, JE
    Fleck, NA
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (1-2) : 95 - 109
  • [34] Fatigue crack growth under cyclic torsional loading
    Martins, Rui F.
    Ferreira, Luis
    Reis, Luis
    Chambel, Paulo
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2016, 85 : 56 - 66
  • [35] Surface crack growth in cylindrical hollow specimen subject to tension and torsion
    Shlyannikov, V.
    Yarullin, R.
    Ishtyryakov, I.
    FRATTURA ED INTEGRITA STRUTTURALE, 2015, (33): : 335 - 344
  • [36] Fatigue crack growth for a surface crack in a round bar under multi-axial loading condition
    Yang, FP
    Kuang, ZB
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2005, 28 (11) : 963 - 970
  • [37] SECONDARY CRACKING DURING SURFACE CRACK-GROWTH UNDER TENSILE FATIGUE LOADING
    BAI, JB
    CHEN, SY
    ENGINEERING FRACTURE MECHANICS, 1988, 30 (02) : 161 - 167
  • [38] Fatigue crack growth from small defects under out-of-phase combined loading
    Endo, M.
    McEvily, A. J.
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (08) : 1529 - 1541
  • [39] Crack growth prediction for irradiated stainless steels under the combined fatigue-creep loading
    Fuller, Robert W.
    Simsiriwong, Jutima
    Shamsaei, Nima
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 109
  • [40] An observation of crack initiation and early crack growth under impact fatigue loading
    Zhang, M
    Yang, PS
    Tan, YX
    Liu, Y
    Gong, SP
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 271 (1-2): : 390 - 394
12345