Role of Ni addition on hydrogen storage characteristics of ZrV2 Laves phase compounds

In this work, the Zr(V1-xNix)(2) (x = 0.02, 0.05, 0.1, 0.15, 0.25) intermetallic compounds were prepared by the arc-melt method and annealed 1273 K for 168 h. The alloys have been characterized for the structure, morphology, pressure composition isotherms over a H-2 pressure range of 150 Pa to 50 MPa at different temperatures, hydrogen storage capacity, hydrogen absorption kinetics in detail. The solidification segregation of as-cast Zr(V1-xNix)(2) alloys almost disappear under the homogenizing treatment at 1273 K for 168 h. With increasing Ni content in the alloys, the hydrogen absorption capacities decrease and equilibrium pressure increases. Meanwhile, the standard enthalpy of formation AH and standard entropy of formation AS for the alloys' hydrides have been obtained from Van't Hoff's equation in the (alpha + beta) two-phase region of Zr(V1-xNix)(2) alloys. It is found that the Zr(V1-xNix)(2) alloys with higher Ni content preserve higher absolute values of AH and more stable metal hydride roughly. The alloys also exhibit fast absorption kinetics at room temperature and 773 K. After 100 hydrogen absorption/desorption cycles, Zr(V0.05Ni0.95)(2) still preserves 94.1% of the first hydrogen storage capacity at 823 K and shows excellent cyclic stability. (C) 2014 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.