Forced Cooling Friction Stir Welding of 2060-T8 Al-Li Alloy

被引：8

作者：

Niu, Shiyu ^{[1
]}

Yue, Yumei ^{[1
]}

Yan, Dejun ^{[2
]}

Ma, Zhongwei ^{[1
]}

Ji, Shude ^{[1
]}

机构：

[1] Shenyang Aerosp Univ, Fac Aerosp Engn, Shenyang 110136, Liaoning, Peoples R China

[2] CSSC Huangpu Wenchong Shipbldg Co Ltd, Guangdong Prov Key Lab Adv Welding Technol Ships, Guangzhou 510715, Guangdong, Peoples R China

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2019年 / 28卷 / 09期

基金：

中国博士后科学基金; 中国国家自然科学基金;

关键词：

2060-T8 Al-Li alloy; forced cooling process; friction stir welding; mechanical properties; MECHANICAL-PROPERTIES; MATERIAL-FLOW; TENSILE PROPERTIES; MICROSTRUCTURE; EVOLUTION; GEOMETRY; BEHAVIOR; SPEED;

D O I：

10.1007/s11665-019-04255-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Friction stir welding of 2060-T8 Al-Li alloy was experimentally investigated. Forced cooling process was realized by placing two copper pressure plates with a waterway on both sides of weld top surface. The relations between joint formation, microstructures and mechanical properties were mainly discussed. Compared with conventional joint by natural cooling, the welding joint with smaller flashes by forced cooling has the smaller well-distributed grains and higher microhardness in the stir zone (SZ). The tensile strength and elongation of forced cooling joint, respectively, reach 445.7 MPa and 6.7%, which are obviously higher than those of the conventional joint. The fracture locations of the conventional and forced cooling joints are located in the SZ, and the fracture surface morphologies show a typical ductile fracture mode.

引用

下载

页码：5763 / 5771

页数：9

共 50 条

[21] Fabrication of third generation Al-Li alloy by friction stir welding: a review
Alam, Md Parwez
Sinha, A. N.
SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES, 2019, 44 (06):
[22] Microstructure evolution and mechanical properties of 2060 Al-Li alloy via friction stir additive manufacturing
Jiang, Tao
Jiao, Tao
Dai, Guoqing
Shen, Zhikang
Guo, Yanhua
Sun, Zhonggang
Li, Wenya
JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 935
[23] The precipitate evolution in friction stir welding of 2195-O Al-Li alloy
Chen, Peng
Li, Tianning
Yin, Xiangrui
Tang, Yang
Liu, Ge
Wang, Shuibo
Huang, Bensheng
Zhang, Zhiqing
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 24 : 1991 - 2006
[24] Microstructural evolution of 2099 Al-Li alloy during friction stir welding process
Lin, Yi
Zheng, Ziqiao
MATERIALS CHARACTERIZATION, 2017, 123 : 307 - 314
[25] Impact of surface state in probeless friction stir spot welding of an Al-Li alloy
Chu, Q.
Yang, X. W.
Li, W. Y.
Lu, T.
Zhang, Y.
Vairis, A.
Wang, W. B.
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2019, 24 (03) : 200 - 208
[26] Investigation on three-roller cylindrical bending of 2060-T8 Al-Li alloy plate for aircraft fuselage skin components
Peng, Jingwen
Li, Weidong
Wan, Min
Zhang, Changsheng
Li, Jian
Sun, Guangai
INTERNATIONAL JOURNAL OF MATERIAL FORMING, 2018, 11 (02) : 269 - 278
[27] Hardenability of 2060 Al-Li alloy
Liu C.
Li J.-F.
Ning H.
Liu D.-Y.
Chen Y.-L.
Zhang X.-H.
Ma P.-C.
Tan C.-Y.
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2019, 29 (11): : 2451 - 2458
[28] Laser scanning welding of 2060 Al-Li alloy with filler wire
Chen G.
Wang B.
Zhong P.
Liu J.
Li W.
Hanjie Xuebao/Transactions of the China Welding Institution, 2020, 41 (04): : 44 - 50
[29] Investigation on three-roller cylindrical bending of 2060-T8 Al-Li alloy plate for aircraft fuselage skin components
Jingwen Peng
Weidong Li
Min Wan
Changsheng Zhang
Jian Li
Guangai Sun
International Journal of Material Forming, 2018, 11 : 269 - 278
[30] A parametric investigation on friction stir welding of Al-Li 2099
Cisko, A. R.
Jordon, J. B.
Amaro, R. L.
Allison, P. G.
Wlodarski, J. S.
McClelland, Z. B.
Garcia, L.
Rushing, T. W.
MATERIALS AND MANUFACTURING PROCESSES, 2020, 35 (10) : 1069 - 1076

← 1 2 3 4 5 →