Forced Cooling Friction Stir Welding of 2060-T8 Al-Li Alloy

被引：8
|
作者：
Niu, Shiyu [1 ]
Yue, Yumei [1 ]
Yan, Dejun [2 ]
Ma, Zhongwei [1 ]
Ji, Shude [1 ]
机构：
[1] Shenyang Aerosp Univ, Fac Aerosp Engn, Shenyang 110136, Liaoning, Peoples R China
[2] CSSC Huangpu Wenchong Shipbldg Co Ltd, Guangdong Prov Key Lab Adv Welding Technol Ships, Guangzhou 510715, Guangdong, Peoples R China
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2019年 / 28卷 / 09期
基金：
中国博士后科学基金; 中国国家自然科学基金;
关键词：
2060-T8 Al-Li alloy; forced cooling process; friction stir welding; mechanical properties; MECHANICAL-PROPERTIES; MATERIAL-FLOW; TENSILE PROPERTIES; MICROSTRUCTURE; EVOLUTION; GEOMETRY; BEHAVIOR; SPEED;
D O I：
10.1007/s11665-019-04255-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Friction stir welding of 2060-T8 Al-Li alloy was experimentally investigated. Forced cooling process was realized by placing two copper pressure plates with a waterway on both sides of weld top surface. The relations between joint formation, microstructures and mechanical properties were mainly discussed. Compared with conventional joint by natural cooling, the welding joint with smaller flashes by forced cooling has the smaller well-distributed grains and higher microhardness in the stir zone (SZ). The tensile strength and elongation of forced cooling joint, respectively, reach 445.7 MPa and 6.7%, which are obviously higher than those of the conventional joint. The fracture locations of the conventional and forced cooling joints are located in the SZ, and the fracture surface morphologies show a typical ductile fracture mode.
引用
下载
收藏
页码：5763 / 5771
页数：9
相关论文
共 50 条
  • [1] Forced Cooling Friction Stir Welding of 2060-T8 Al-Li Alloy
    Shiyu Niu
    Yumei Yue
    Dejun Yan
    Zhongwei Ma
    Shude Ji
    Journal of Materials Engineering and Performance, 2019, 28 : 5763 - 5771
  • [2] Friction stir welding of 2060-T8 Al-Li alloy. Part II: Tensile fracture behavior
    Tao, Y.
    Zhang, Z.
    Yu, B. H.
    Xue, P.
    Ni, D. R.
    Xiao, B. L.
    MATERIALS CHARACTERIZATION, 2020, 168
  • [3] COMPARATIVE STUDY OF 2060-T8 Al-Li ALLOY FRICTION STIR WELDED JOINTS BETWEEN NATURAL COOLING AND WATER COOLING
    Ma, Lin
    Niu, Shiyu
    Ji, Shude
    Gong, Peng
    ARCHIVES OF METALLURGY AND MATERIALS, 2020, 65 (01) : 305 - 312
  • [4] Friction stir welding of 2060-T8 Al-Li alloy. Part I: Microstructure evolution mechanism and mechanical properties
    Tao, Y.
    Zhang, Z.
    Yu, B. H.
    Xue, P.
    Ni, D. R.
    Xiao, B. L.
    Ma, Z. Y.
    MATERIALS CHARACTERIZATION, 2020, 168
  • [5] An effect of the rotation speed on microstructure and mechanical properties of the friction stir welded 2060-T8 Al-Li alloy
    Liu, Huijie
    Hu, Yanying
    Dou, Chao
    Sekulic, Dusan P.
    MATERIALS CHARACTERIZATION, 2017, 123 : 9 - 19
  • [6] Interface structure and mechanical properties of friction stir welding joint of 2099-T83/2060-T8 dissimilar Al-Li alloys
    State Key Laboratory of Solidification, Shaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi'an
    710072, China
    不详
    100024, China
    Jinshu Xuebao, 3 (281-288):
  • [7] INTERFACE STRUCTURE AND MECHANICAL PROPERTIES OF FRICTION STIR WELDING JOINT OF 2099-T83/2060-T8 DISSIMILAR Al-Li ALLOYS
    Liu Fenjun
    Fu Li
    Zhang Wenyuan
    Meng Qiang
    Dong Chunlin
    Luan Guohong
    ACTA METALLURGICA SINICA, 2015, 51 (03) : 281 - 288
  • [8] Salt Spray Corrosion of 2060-T8 Al-Li Alloy in an Aggressive Environment
    Zhang, Zhengquan
    Wang, Yuling
    Li, Liangfen
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2022, 2022
  • [9] Interface characteristic and tensile property of friction stir lap welding of dissimilar aircraft 2060-T8 and 2099-T83 Al-Li alloys
    Meng, Xiangchen
    Xu, Zheng
    Huang, Yongxian
    Xie, Yuming
    Wang, Yaobin
    Wan, Long
    Lv, Zongliang
    Cao, Jian
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 94 (1-4): : 1253 - 1261
  • [10] Effect of Trailing Intensive Cooling on Residual Stress and Welding Distortion of Friction Stir Welded 2060 Al-Li Alloy
    Ji, Shude
    Yang, Zhanpeng
    Wen, Quan
    Yue, Yumei
    Zhang, Liguo
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (05) : 397 - 403
12345