ANALYSIS OF THE HEATING OF STEEL WIRES DURING HIGH SPEED MULTIPASS DRAWING PROCESS

The analysis of the heating of the wire including theoretical studies showed that in the multistage drawing process a increase drawing speed causes intense heating of a thin surface layer of the wire to a temperature exceeding 1100 degrees C, which should be explained by the accumulation of heat due to friction at the interface between wire and die. It has been shown that with increasing of drawing speed the heated surface layer thickness measured at the exit of the wire from the dies is reduced significantly and at drawing speed of 25 m/s is equal to about 68 mu m. The decrease in the thickness of this layer can be explained by a shorter time of heat transfer to the wire, which causes additional heat accumulation in the surface layer. Thus fivefold increase in drawing speed caused an approximately 110% increase in the temperature in the surface layer of the wire. Experimental studies have shown that the increase of drawing speed of 5 to 25 m/s will increase the temperature of the wire after coiled on the spool more than 400%.