Crevice and pitting corrosion of low temperature plasma nitrided UNS S32750 super duplex stainless steel

被引：30
|
作者：
Calabokis, Oriana Palma [1 ]
de la Rosa, Yamid Nunez [1 ]
Lepienski, Carlos M. [1 ]
Cardoso, Rodrigo Perito [2 ]
Borges, Paulo Cesar [1 ]
机构：
[1] Univ Tecnol Fed Parana UTFPR, Curitiba, Parana, Brazil
[2] Univ Fed Santa Catarina UFSC, Florianopolis, SC, Brazil
来源：
SURFACE & COATINGS TECHNOLOGY | 2021年 / 413卷 / 413期
关键词：
Super duplex stainless steel (SDSS); Low temperature plasma nitriding (LTPN); Pitting corrosion; Crevice corrosion; NITROGEN; RESISTANCE; BEHAVIOR; MICROSTRUCTURE; REPASSIVATION; ENHANCEMENT; SINGLE; S31803; NACL;
D O I：
10.1016/j.surfcoat.2021.127095
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The UNS 532750 super duplex stainless steel (SDSS) was low temperature plasma nitrided at 350 degrees C and 400 degrees C for 4 h. Pitting and crevice corrosion resistance was evaluated using electrochemical techniques in a NaCl neutral solution. Nitriding treatments resulted in increased in hardness, general corrosion resistance and in the passive layer breakdown potential. Regarding crevice corrosion tests, the nitrided surfaces showed lower current densities during the potentiostatic polarization and lower corrosion depths when compared to the untreated surface. The nitrogen played a fundamental role in the passivation behavior and in the susceptibility to repassivation of localized corrosion.
引用
收藏
页数：13
相关论文
共 50 条
  • [31] Effect of inorganic anions on the corrosion behavior of UNS S32750 duplex stainless steel in chloride solution
    Jin, S.
    Liu, C. -M.
    Lin, X.
    Li, M. -J.
    Cao, H. -B.
    Wang, H. -Z.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (10): : 1077 - 1083
  • [32] Effect of Aging Temperature on the Microstructure, Local Mechanical Properties, and Wear Behavior of a UNS S32750 Super Duplex Stainless Steel
    Bouzid Maamache
    Billel Cheniti
    Brahim Belkessa
    Karima Tahar-chaouch
    Ramdhane Kouba
    Journal of Materials Engineering and Performance, 2021, 30 : 546 - 555
  • [33] Analysis of Pitting Corrosion Resistance in Welding Repair by GTAW Procedure in a Superduplex Stainless Steel UNS S32750)
    de Souza, Juliana Primo Basílio
    Arias, Alexandre de Gouvêa
    Pardal, Juan Manuel
    Mainier, Fernando Benedicto
    Ferreira, Miguel Luiz Ribeiro
    Tavares, Sérgio Souto Maior
    Soldagem e Inspecao, 2011, 16 (02): : 104 - 113
  • [34] Multivariable Statistical Analysis of the Pulsed Laser Welding of UNS S32750 Super Duplex Stainless Steel (SDSS)
    Saravanan, S.
    Sivagurumanikandan, N.
    Raghukandan, K.
    LASERS IN ENGINEERING, 2021, 48 (4-6) : 305 - 316
  • [35] Microstructure Evolution during Hot Deformation of UNS S32750 Super-Duplex Stainless Steel Alloy
    Cojocaru, Elisabeta Mirela
    Nocivin, Anna
    Raducanu, Doina
    Angelescu, Mariana Lucia
    Cinca, Ion
    Balkan, Irina Varvara
    Serban, Nicolae
    Cojocaru, Vasile Danut
    MATERIALS, 2021, 14 (14)
  • [36] Analysis of Pitting Corrosion Resistance in Welding Repair by GTAW Procedure in a Superduplex Stainless Steel UNS S32750
    Basilio de Souza, Juliana Primo
    Arias, Alexandre de Gouvea
    Pardal, Juan Manuel
    Mainier, Fernando Benedicto
    Ribeiro Ferreira, Miguel Luiz
    Major Tavares, Sergio Souto
    SOLDAGEM & INSPECAO, 2011, 16 (02): : 104 - 113
  • [37] Effect of Aging Temperature on the Microstructure, Local Mechanical Properties, and Wear Behavior of a UNS S32750 Super Duplex Stainless Steel
    Maamache, Bouzid
    Cheniti, Billel
    Belkessa, Brahim
    Tahar-chaouch, Karima
    Kouba, Ramdhane
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (01) : 546 - 555
  • [38] Investigation of stress corrosion cracks in a UNS S32750 superduplex stainless steel
    Tavares, S. S. M.
    Silva, V. G.
    Pardal, J. M.
    Corte, J. S.
    ENGINEERING FAILURE ANALYSIS, 2013, 35 : 88 - 94
  • [39] Influence of Cations on the Corrosion of UNS S32750 Stainless Steel in Media with Chloride
    Rodrigues, Vinicius de O.
    de Carvalho, Marcos Paulo M.
    de Andrade, Monica C.
    Bastos, Ivan N.
    REVISTA VIRTUAL DE QUIMICA, 2013, 5 (04) : 678 - 690
  • [40] Hydrogen induced stress cracking in UNS S32750 super duplex stainless steel tube weld joint
    da Silva, B. R. S.
    Salvio, F.
    dos Santos, D. S.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2015, 40 (47) : 17091 - 17101
12345