Composition Distribution and Electrochemical Behavior of an Ni2Al3 Coating on Q235 Steel

被引：12
|
作者：
Li, Ningning [1 ]
Wang, Minzhi [1 ]
Zheng, Gong [1 ]
Li, Yongsheng [1 ]
Chen, Guang [1 ]
机构：
[1] Nanjing Univ Sci & Technol, Minist Educ, Engn Res Ctr Mat Behav & Design, Nanjing 210094, Jiangsu, Peoples R China
来源：
METALS | 2016年 / 6卷 / 03期
关键词：
Ni2Al3; coating; polarization curve; electrochemical impedance spectroscopy; pitting corrosion; ALUMINIDE/NICKEL HYBRID COATINGS; 3.5-PERCENT NACL SOLUTION; CORROSION BEHAVIOR; NI3AL COATINGS; CARBON-STEEL; ALLOY-STEELS; NICKEL; OXIDATION; MICROSTRUCTURES; ENVIRONMENTS;
D O I：
10.3390/met6030058
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An Ni2Al3 coating was prepared via the electrodeposition of nickel followed by pack aluminization. Polarization curve and electrochemical impedance spectroscopy were performed to study the room temperature corrosion behavior of the coating in a 3.5 wt. % NaCl solution. The long-term impedance of the coating was also investigated after immersion for 30 days. Results show that the Ni2Al3 coating possessed lower corrosion current density (I-corr) and higher polarization resistance (R-p) than the substrate in the solution. The Bode plots of the coating showed two time constants after the long-term immersion. Pitting corrosion was found on the coating surface.
引用
收藏
页数：8
相关论文
共 50 条
  • [21] Effects of Pitting Corrosion on the Fatigue Behavior of Q235 Steel
    Shanhua Xu
    Songbo Ren
    Youde Wang
    Journal of Harbin Institute of Technology(New series), 2017, (01) : 81 - 90
  • [22] STUDY ON CORROSION BEHAVIOR OF Q235 STEEL AND 16MN STEEL BY ELECTROCHEMICAL AND WEIGHT LOSS METHOD
    Quan, Bianli
    Xie, Zhiping
    ARCHIVES OF METALLURGY AND MATERIALS, 2023, 68 (02) : 531 - 540
  • [23] Corrosion Behavior of High-Pressure Cold-Sprayed Zn30Al Alloy Coating on Q235 Steel
    Ding, Xiang
    Wu, Kunze
    Li, Ruiqi
    Wang, Qun
    Liang, Xingxin
    Yuan, Chengqing
    Yuan, Zhennan
    Ramachandran, Chidambaram Seshadri
    COATINGS, 2024, 14 (11)
  • [24] Corrosion protection of a novel SiO2@PANI coating for Q235 carbon steel
    Shi, Shuanger
    Zhao, Yunyan
    Zhang, Zhiming
    Yu, Liangmin
    PROGRESS IN ORGANIC COATINGS, 2019, 132 (227-234) : 227 - 234
  • [25] The electrochemical behavior of corrosion and passivation for Q235 carbon steel in acidic phosphate buffer solutions without and with NO2-
    Hu, Xiaochen
    Zhang, Pei
    Zhou, Yong
    Yan, Fuan
    ANTI-CORROSION METHODS AND MATERIALS, 2020, 67 (05) : 473 - 481
  • [26] Laser-Melted Wc/Ni-Based Coating Remelting Study on Q235 Steel Surface
    Wu, Xianglin
    Chen, Junhao
    Huang, Jiang
    Shi, Wenqing
    Wang, Qingheng
    An, Fenju
    Wu, Jingquan
    COATINGS, 2024, 14 (09)
  • [27] Effects of electrochemical corrosion characteristis on electrochemical cold drawing of Q235 steel bar
    Chen, T. J.
    Yang, B. Q.
    Li, B.
    Guo, J. L.
    Zhang, P.
    Cao, X. Z.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2020, 275
  • [28] Corrosion Performance of Epoxy/Sulfur-Selenium Coating on Q235 Steel
    Meng, Konglan
    Wei, Wei
    Wei, Kunxia
    Alexandrov, Igor V.
    An, Xulong
    Wang, Dandan
    Liu, Xiangkui
    COATINGS, 2024, 14 (03)
  • [29] Corrosion of Carbon Steel Q235 in a Crevice Under a Simulated Disbonded Coating
    Xu, Jin
    Sun, Cheng
    Yan, Maocheng
    Wang, Fuhui
    CORROSION, 2014, 70 (07) : 686 - 694
  • [30] Initial corrosion behavior of carbon steel Q235 in the atmosphere with SO2
    Wang Chuan
    Wang Zhenyao
    Ke Wei
    ACTA METALLURGICA SINICA, 2008, 44 (06) : 729 - 734
12345