Effect of homogenization treatment and silicon content on the microstructure and hot workability of dilute Al-Fe-Si alloys

被引:48
|
作者
Shakiba, M. [1 ]
Parson, N. [2 ]
Chen, X. -G. [1 ]
机构
[1] Univ Quebec Chicoutimi, Dept Appl Sci, Saguenay, PQ G7H 2B1, Canada
[2] Rio Tino Alcan, Arvida Res & Dev Ctr, Saguenay, PQ G7S 4K8, Canada
基金
加拿大自然科学与工程研究理事会;
关键词
1xxx aluminum alloys; Homogenization; Flow stress; Solid-state phase transformation; Hot workability; INTERMETALLIC PHASES; PRECIPITATION; BEHAVIOR;
D O I
10.1016/j.msea.2014.09.072
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The effect of the homogenization treatment on the microstructure and hot workability of two dilute Al-Fe-Si alloys was investigated using optical microscopy, SEM, EBSD, electrical conductivity measurements and hot compression testing. Homogenization promoted the phase transformation from the metastable AlmFe or alpha-AlFeSi phase to the Al3Fe equilibrium phase and induced a significant change in solute levels in the solid solution. The Al3Fe dissolved and transformed completely at 550 degrees C in both alloys. The a-AlFeSi was transformed at 590 degrees C in the low Si alloy (Al-03Fe-0.1Si), whereas it began to decompose and transform to Al3Fe at 630 degrees C in the high Si alloy (Al-0.3Fe-0.25Si). The flow stress behavior of dilute Al-Fe-Si alloys was primarily controlled by the amount of Fe and Si in the solid solution. Homogenization at 550 degrees C significantly reduced the solid solution levels due to the elimination of the supersaturation originating from the cast ingot and produced the lowest flow stress under all of the deformation conditions studied. An increase in the homogenization temperature from 550 to 630 degrees C increased the flow stress by 10-23% and 15-45% for the low Si alloy and the high Si alloy, respectively, over the range of deformation conditions examined. An increase in the silicon level from 0.10% to 0.25% raised the overall flow stresses by 4-11% due to increased solute levels for given homogenization conditions. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:180 / 189
页数:10
相关论文
共 50 条
  • [21] Dissolution behavior of Al-Fe-Si alloys at NaOH etching treatment
    Seri, Osami
    Furumata, Kazunao
    Tagashira, Kohsuke
    Keikinzoku/Journal of Japan Institute of Light Metals, 1994, 44 (06): : 315 - 319
  • [22] Effect of cooling rate on the solidification behaviour of Al-Fe-Si alloys
    Dutta, B
    Rettenmayr, M
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 283 (1-2): : 218 - 224
  • [23] On the influence of iron and silicon content on the phase composition of the Al-Fe-Si system
    Andreyachshenko, V. A.
    Toleuova, A. R.
    KOMPLEKSNOE ISPOLZOVANIE MINERALNOGO SYRA, 2025, 332 (01): : 98 - 107
  • [24] Hot deformation behavior and rate-controlling mechanism in dilute Al-Fe-Si alloys with minor additions of Mn and Cu
    Shakiba, M.
    Parson, N.
    Chen, X. -G.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 636 : 572 - 581
  • [25] Effect of Si content on the microstructure and properties of Al–Si alloys fabricated using hot extrusion
    Pan Ma
    Yandong Jia
    Konda Gokuidoss Prashanth
    Zhishui Yu
    Chonggui Li
    Jian Zhao
    Shanglei Yang
    Lixin Huang
    Journal of Materials Research, 2017, 32 : 2210 - 2217
  • [26] Effect of homogenization on recrystallization in a twin-roll cast Al-Fe-Si alloy
    Birol, Yuecel
    JOURNAL OF MATERIALS SCIENCE, 2008, 43 (13) : 4652 - 4657
  • [27] Al-Fe-Si (Aluminum-Iron-Silicon)
    Raghavan, V.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2012, 33 (04) : 322 - 326
  • [28] Al-Fe-Si (Aluminum-Iron-Silicon)
    Raghavan, V.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2009, 30 (02) : 184 - 188
  • [29] Al-Fe-Si (Aluminum-Iron-Silicon)
    V. Raghavan
    Journal of Phase Equilibria and Diffusion, 2011, 32 : 140 - 142
  • [30] Al-Fe-Si (Aluminum-Iron-Silicon)
    V. Raghavan
    Journal of Phase Equilibria and Diffusion, 2009, 30 : 184 - 188