Comparison between nanoindentation and scratch test hardness (scratch hardness) values of copper thin films on oxidised silicon substrates

被引：85
|
作者：
Beegan, D.
Chowdhury, S.
Laugier, M. T. [1 ]
机构：
[1] Univ Limerick, Dept Phys, Limerick, Ireland
[2] Univ Alabama Birmingham, Dept Phys, Birmingham, AL 35294 USA
来源：
SURFACE & COATINGS TECHNOLOGY | 2007年 / 201卷 / 12期
关键词：
scratch test; nanoindentation; copper; hardness;
D O I：
10.1016/j.surfcoat.2006.10.031
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In this paper we measured for the first time the scratch hardness of copper thin films and compared this with hardness measured from nanoindentation. Copper films with thicknesses in the range 100 nm to 500 nm were deposited by rf magnetron sputtering on silicon substrates. Scratch hardness was determined by CSM (TM) scratch tester using scratch widths at low loads. The measured hardness values were compared with conventional nanoindentation hardness measurement by CSM (TM) nanohardness tester. At these low indentation depths there is a good correlation between the scratch hardness and the nanoindentation hardness, with an increase in hardness as the film thickness decreases. (c) 2006 Elsevier B.V All rights reserved.
引用
收藏
页码：5804 / 5808
页数：5
相关论文
共 23 条
  • [21] Hardness measurements at shallow depths on ultra-thin amorphous carbon films deposited onto silicon and Al2O3-TiC substrates
    Lemoine, P
    Zhao, JF
    Quinn, JP
    McLaughlin, JA
    Maguire, P
    THIN SOLID FILMS, 2000, 379 (1-2) : 166 - 172
  • [22] A comparison between the corrosion behavior of nanostructured copper thin films deposited on oxidized silicon and copper sheet in alkaline media
    Yeganeh, M.
    Saremi, M.
    SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07): : 2218 - 2224
  • [23] Heteroepitaxial silicon thin films on flexible polycrystalline metal substrates for crystalline photovoltaic solar cells: A comparison between physical vapor deposition and plasma-enhanced chemical vapor deposition
    Gao, Ying
    Dutta, Pavel
    Rathi, Monika
    Yao, Yao
    Iliev, Milko
    Ryou, Jae-Hyun
    Selvamanickam, Venkat
    2014 IEEE 40TH PHOTOVOLTAIC SPECIALIST CONFERENCE (PVSC), 2014, : 1287 - 1291
123