The influence of Nb on hot corrosion behavior of Ni-based superalloy at 800 °C in a mixture of Na2SO4-NaCl

被引：21

作者：

Weng, Fei ^{[1
]}

Yu, Huijun ^{[2
]}

Wan, Kai ^{[1
]}

Chen, Chuanzhong ^{[1
]}

机构：

[1] Shandong Univ, Dept Mat Sci & Engn, Key Lab Liquid Solid Struct Evolut & Proc Mat, Minist Educ, Jinan 250061, Shandong, Peoples R China

[2] Shandong Univ, Sch Mech Engn, Key Lab High efficiency & Clean Mech Manufacture, Minist Educ, Jinan 250061, Shandong, Peoples R China

来源：

JOURNAL OF MATERIALS RESEARCH | 2014年 / 29卷 / 21期

关键词：

HIGH-TEMPERATURE CORROSION; SINGLE-CRYSTAL SUPERALLOYS; FE-BASED SUPERALLOYS; OXIDATION BEHAVIOR; MECHANICAL-PROPERTIES; SO2-O2; ATMOSPHERES; NI-5AL COATINGS; AL-ALLOY; 900-DEGREES-C; RESISTANCE;

D O I：

10.1557/jmr.2014.282

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

New-type Ni-based superalloys with and without Nb were designed in this study. Their hot corrosion behaviors were investigated at 800 degrees C with the deposition of a mixture of Na2SO4 and NaCl. The corrosion kinetics was studied by thermogravimetry. Microstructure of the corrosion scales was studied by SEM and the phase constituent was analyzed by XRD. Results showed that the corrosion kinetics followed approximately parabolic law. The corrosion scales on the two Ni-based alloys were comprised of Cr2O3, Al2O3, TiO2, and NiCr2O4. NiO was only detected in the scale on alloy without Nb. Nb2O5 appeared with the addition of 2.0 wt% Nb. No sulfide emerged in the scales. The corrosion scales both exhibited a layered structure. With Nb addition, the hot corrosion resistance of the alloy was notably improved. The action mechanism of Nb was investigated extensively in this study.

引用

页码：2596 / 2603

页数：8

共 50 条

[41] Hot corrosion behavior of Pt plus Hf co-modified NiAl coating in the mixed salt of Na2SO4-NaCl at 900 °C
Yang, Y. F.
Liu, Z. L.
Ren, P.
Wang, Q. W.
Bao, Z. B.
Zhu, S. L.
Li, W.
CORROSION SCIENCE, 2020, 167
[42] Hot Corrosion Performance of Single-Crystal CMSX-4 and CMSX-486 Superalloys in the Mixture of Na2SO4-NaCl Melts
K. M. Oluwasegun
O. O. Ajide
T. Tanaka
L. Zhang
O. A. Ojo
Journal of Materials Engineering and Performance, 2019, 28 : 5509 - 5520
[43] Influence of grain size on the corrosion behavior of a Ni-based superalloy nanocrystalline coating in NaCl acidic solution
Liu, Li
Li, Ying
Wang, Fuhui
ELECTROCHIMICA ACTA, 2008, 53 (05) : 2453 - 2462
[44] Role of Temperature in Na2SO4-K2SO4 Deposit Induced Type II Hot Corrosion of NiAl Coating on a Commercial Ni-Based Superalloy
Wang, Yaping
Pillai, Rishi
Yazhenskikh, Elena
Frommherz, Martin
Mueller, Michael
Naumenko, Dmitry
ADVANCED ENGINEERING MATERIALS, 2020, 22 (06)
[45] Hot Corrosion Behavior of Fe-Cr-Ni-Based Austenitic Heat-Resistant Steel Weld Metal in Na2SO4-NaCl Molten Salts at Different Temperatures
Xu, Zhang
Wan, Jinchu
Yang, Zonghui
Hui, Zhou
Cong, Pan
Chu, Yajie
Li, Xiaoquan
HIGH TEMPERATURE CORROSION OF MATERIALS, 2023, 99 (1-2) : 117 - 132
[46] Hot corrosion behavior of AlCuFeCr quasicrystalline coating on titanium alloy with the mixture of NaCl and Na2SO4 deposit
Wang, Fengfeng
Zhou, Chungen
Gong, Shengkai
Xu, Huibin
2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2313 - +
[47] HOT CORROSION BEHAVIOR OF NIMONIC-105 IN NACL AND NA2SO4
KAMESWARI, S
WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1989, 40 (04): : 213 - 218
[48] Hot corrosion of surface-modified Sm2Co17 high-temperature magnet with Ni and Ni/Cr bilayer coatings in 75 wt% Na2SO4-NaCl mixture
Bibi, Saira
Wang, Jing-Min
Mehmood, Tariq
Khan, Waheed Qamar
Jiang, Cheng-Bao
RARE METALS, 2021, 40 (09) : 2494 - 2500
[49] Hot corrosion behaviour of plasma sprayed coatings on a Ni-based superalloy in Na2SO4-60%V2O5 environment
Prakash, S
Puri, D
Singh, H
ISIJ INTERNATIONAL, 2005, 45 (06) : 886 - 895
[50] Hot corrosion behavior of powder metallurgy Rene95 nickel-based superalloy in molten NaCl-Na2SO4 salts
Lei Zheng
Zhang Maicang
Dong Jianxin
MATERIALS & DESIGN, 2011, 32 (04): : 1981 - 1989

← 1 2 3 4 5 →