Microstructure and strength of rapidly solidified and extruded Mg-Zn alloys

被引：93
|
作者：
Maeng, DY [1 ]
Kim, TS
Lee, JH
Hong, SJ
Seo, SK
Chun, BS
机构：
[1] Chungnam Natl Univ, Rapidly Solidified Mat Res Ctr, Taejon 305764, South Korea
[2] Taedok Coll, Ind Liason Off 48, Taejon 305715, South Korea
来源：
SCRIPTA MATERIALIA | 2000年 / 43卷 / 05期
关键词：
flake; rapid solidification; cooling rate; twin rolling; precipitation hardening;
D O I：
10.1016/S1359-6462(00)00428-0
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Rapidly solidified Mg-(3,6)wt%Zn binary alloy flakes were manufactured by twin roll process and extruded. Microstructural change of the as solidified flake and the extruded bar was dependent on the composition, cooling rate and heat treating. Grain size was reduced from 125 μm in as cast alloy to 10 μm by rapid solidification, resulting in the hardness increase. Using the secondary dendrite arm spacing in the microstructure of the flake, cooling rate during the twin rolling was calculated as 2×103 K/s. Strength of the both alloy bars was measured to increase by forming MgZn′ precipitates during aging at 473 K for 15 hrs.
引用
收藏
页码：385 / 389
页数：5
相关论文
共 50 条
  • [21] Thermal conductivity of as-cast and as-extruded binary Mg-Zn alloys
    Ying, T.
    Zheng, M. Y.
    Li, Z. T.
    Qiao, X. G.
    Xu, S. W.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 621 : 250 - 255
  • [22] Research progresses of high strength Mg-Zn series alloys
    Zhang, Ding-Fei
    Qi, Fu-Gang
    Zhao, Xia-Bing
    Shi, Guo-Liang
    Dai, Qing-Wei
    Chongqing Daxue Xuebao/Journal of Chongqing University, 2010, 33 (11): : 53 - 61
  • [23] Microstructure characterisation and mechanical properties of rapidly solidified Mg-Zn-Ca alloys with Ce addition
    Chen, Z. H.
    Zhou, T.
    Chen, D.
    Yan, H. G.
    Chen, J. H.
    MATERIALS SCIENCE AND TECHNOLOGY, 2008, 24 (07) : 848 - 855
  • [24] RAPIDLY SOLIDIFIED MG-AL-ZN-RARE EARTH ALLOYS
    CHANG, CF
    DAS, SK
    RAYBOULD, D
    JOURNAL OF MATERIALS ENGINEERING, 1987, 9 (02) : 141 - 146
  • [25] Microstructures and properties of rapidly solidified Mg-Zn-Ca alloys
    School of Materials Science and Engineering, Hunan University, Changsha 410082, China
    Trans Nonferrous Met Soc China, 2008, SPEC. ISSUE 1 (s101-s106):
  • [26] Microstructures and phase selection in rapidly solidified Zn-Mg alloys
    Akdeniz, MV
    Wood, JV
    JOURNAL OF MATERIALS SCIENCE, 1996, 31 (02) : 545 - 550
  • [27] Microstructures and properties of rapidly solidified Mg-Zn-Ca alloys
    周涛
    陈鼎
    陈振华
    Transactions of Nonferrous Metals Society of China, 2008, 18 (S1) : 101 - 106
  • [28] Mechanical properties of rapidly solidified Mg-Al-Zn alloys
    Daloz, D
    Michot, G
    Steinmetz, P
    INTERNATIONAL JOURNAL OF RAPID SOLIDIFICATION, 1996, 9 (03): : 171 - 186
  • [29] Superplastic properties of rapidly solidified Mg-Al-Zn alloys
    Kaneko, J
    Sugamata, M
    Hisata, N
    TOWARDS INNOVATION IN SUPERPLASTICITY II, 1999, 304-3 : 85 - 90
  • [30] Microstructures and properties of rapidly solidified Mg-Zn-Ca alloys
    Zhou Tao
    Chen Ding
    Chen Zhen-hua
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 : S101 - S106
12345