In vivo and in vitro evaluation of effects of Mg-6Zn alloy on apoptosis of common bile duct epithelial cell

Biodegradable magnesium alloy implants have attracted much attention because of their excellent biocompatibility and good mechanical properties. However, effects of Mg alloy on cell apoptosis remain unclear. The aim of this study was to investigate the effects of the Mg-6Zn alloy on the apoptosis and necrosis of common bile duct (CBD) epithelial cells. In the in vitro experiments, primary mouse extrahepatic bile epithelial cells (MEBECs) were exposed to Mg-6Zn alloy extracts with different concentrations (0, 40, 80, and 100 %). Flow cytometry analysis indicated that low concentration Mg-6Zn extract can induce apoptosis of MEBECs, and high concentration Mg-6Zn extracts may relate to necrosis and/or 'apoptotic necrosis'. Real-time PCR results showed that when MEBECs were treated with 40 % extracts for 3 days, the relative apoptotic genes including Bax, Bax/Bcl-2 ratio, NF-kappa B and caspase-3 were higher than those in the control group. In the in vivo experiments, Mg-6Zn alloy stents were implanted into rabbits' CBD for 1, 2, 3 weeks, respectively. Based on the hematoxylin and eosin (H&E) staining of peri-implant CBD tissue, no apoptotic bodies and necrotic cells were observed. Results of immunohistochemical staining also showed Mg-6Zn stents did not increase expression levels of apoptosis related gene such as Bax, Bcl-2, Bax/Bcl-2 ratio, TNF-alpha, NF-kappa B and caspase-3 in CBD, which indicating Mg-6Zn did not induce significant apoptosis in the in vivo experiments. The different results of in vitro and in vivo experiment may result from the low corrosion rate of Mg-6Zn alloy stents in vivo and local Mg2+ ion concentration in CBD.